Research Article
Correlation of Polymerization Conditions with Thermal and Mechanical Properties of Polyethylenes Made with Ziegler-Natta Catalysts
Table 4
Results of mechanical testing for polyethylene samples.
| Sample | | | Temp. | Time | Modulus | Yield stress | Yield strain | Strain at break | Tensile strength | (bar) | (bar) | (°C) | (hour) | (MPa) | (MPa) | (%) | (%) | (MPa) |
| 1 | 5 | 0 | 60 | 0.5 | | | 4 | | | 2 | 5 | 0 | 60 | 1 | | | 4 | | | 3 | 5 | 0 | 80 | 0.5 | | | 4 | | | 4 | 5 | 0 | 80 | 1 | | | 4 | | | 5 | 5 | 2 | 60 | 0.5 | | | 4 | | | 6 | 5 | 2 | 60 | 1 | | | 4 | | | 7 | 5 | 2 | 80 | 0.5 | | | 4 | | | 8 | 5 | 2 | 80 | 1 | | | 4 | | | 9 | 5 | 5 | 60 | 0.5 | | | 4 | | | 10 | 5 | 5 | 60 | 1 | | | 4 | | | 11 | 5 | 5 | 80 | 0.5 | | | 3 | | | 12 | 5 | 5 | 80 | 1 | | | 4 | | | 13 | 10 | 0 | 60 | 0.5 | | | 4 | | | 14 | 10 | 0 | 60 | 1 | | | 3.6 | | | 15 | 10 | 0 | 80 | 0.5 | | | 4.0 | | | 16 | 10 | 0 | 80 | 1 | | | 3.8 | | | 17 | 10 | 2 | 60 | 0.5 | | | 3.8 | | | 18 | 10 | 2 | 60 | 1 | | | 3.7 | | | 19 | 10 | 2 | 80 | 0.5 | | | 4 | | | 20 | 10 | 2 | 80 | 1 | | | 3 | | | 21 | 10 | 5 | 60 | 0.5 | | | 3 | | | 22 | 10 | 5 | 60 | 1 | | | 3.5 | | | 23 | 10 | 5 | 80 | 0.5 | | | 3 | | | 24 | 10 | 5 | 80 | 1 | | | 3.5 | | |
|
|