Third-Order Nonlinear Optical Behavior of Novel Polythiophene Derivatives Functionalized with Disperse Red 19 Chromophore
Table 2
Comparative analysis of
value obtained by THG and
or
values obtained by
-scan technique.
| Polymers | measured through THG | or by -scan | Reference |
| Poly(thiophene azines) | 5.4 × 10−11 esu at 1550 nm (5 ns pulses) | | [42] |
| Polythiophene derivative | 2 × 10−11 esu at 2100 nm (4 ns pulses) | | [43] |
| Push-pull azobenzene polymers | 1.7 × 10−11 esu at 1064 nm (30 ps pulses) | | [36] |
| Regioregular P3HT | | = 300 GM (per repeated unit) at 800 nm (fs pulses) | [32] |
| Azopolymer derived RD1 | | = −60.1 cm/GW at 532 nm (ps pulses) | [37] |
| Polyoxadiazoles | | = −19.96 cm/GW at 532 nm (ps pulses) | [44] |
| P1 | 6.7 × 10−12 esu at 1300 nm (8 ns pulses) | = −0.63 cm/GW, = 233 GM (per repeated unit) at 800 nm (fs pulses) | This work |
| P2 | 3.1 × 10−12 esu at 1300 nm (8 ns pulses) | = −0.54 cm/GW, = 194 GM (per repeated unit) at 800 nm (fs pulses) | This work |
|
|