Carbon Fiber Composites of Pure Polypropylene and Maleated Polypropylene Blends Obtained from Injection and Compression Moulding
Table 1
Crystallisation properties of the samples.
| Sample | Heating and cooling rate | 10 C/min | 50 C/min | , C | , C | , J/g | , C | , C | , J/g |
| Pure PP | 156.45 | 116.07 | 91.21 | 158.75 | 107.12 | 75.97 | 1 pph CF | 161.41 | 116.12 | 78.78 | 160.1 | 105.47 | 61.34 | 3 pph CF | 158.62 | 117.1 | 74.5 | 157.84 | 107.19 | 60.06 | 5 pph CF | 157.58 | 118.66 | 72.77 | 156.53 | 109.73 | 58.94 |
| PP/PP-g-MAH | 156.42 | 113.24 | 72.99 | 158.03 | 103.99 | 70.83 | 1 pph CF | 157.58 | 118.66 | 90.77 | 156.53 | 109.73 | 59.94 | 3 pph CF | 157.09 | 118.46 | 83.53 | 159.43 | 110.01 | 62.93 | 5 pph CF | 159.37 | 119.48 | 75.38 | 159.69 | 111.05 | 64.12 |
|
|