Review Article
Rice Husk Filled Polymer Composites
Table 3
Mechanical properties of RH filled PE composites.
| Matrix | RH (wt%) | Secondary filler (wt%) | Coupling agent or compatibilizer | Tensile strength (MPa) | Tensile modulus (GPa) | Flexural strength (MPa) | Flexural modulus (GPa) |
Impact strength (Jm−1) (% incr.) | Reference | (wt%) | (% incr.) | (% incr.) | (% incr.) | (% incr.) | Not. | Unnot. |
| HDPE | 65 | — | — | 13.5 | 2.39 | 33.5 | 2.90 | 26 | 38 | [19] |
| HDPE | 65 | — | E-GMA (2.5) | 22.5 | 2.37 | 49.06 | 3.32 | 28 | 65 | [19] |
| HDPE | 65 | — | ethylene-acrylic ester-maleic anhydride (2.5) | 20.9 (55) | 2.42 (1.30) | 40.2 (13.5) | 2.81 (−3.1) | — | 80 (111) | [20] |
| HDPE | 30 | — | Ultra-Plast TP10 (1) | — | — | — | — | — | 75 (−32) | [40] |
| HDPE | 50 | — | MAPE (2) | 25.64 | 2.5 | — | — | 18.39 | — | [41] |
| HDPE | 50 |
MMT (2) | MAPE (2) | 29.83 | 3.2 | — | — | 17.82 | — | [41] |
| rHDPE | 45 | Sawdust (17.1) | MAPP (7.9) | 7.5 | 0.6 | — | — | 15.20 | — | [35] |
| rHDPE | 44.5 | Sawdust (17.1) | MAPP (7.9) | 11.6 | 1.02 | — | — | 33.20 | — | [35] |
| rHDPE/rPET (75/25) | 60 | — | MAPE (3)/E-GMA (5) | 23 (15) | 1.55 (89) | 35 (17) | 3.5 (192) | 25 (−69) | — | [12] |
|
|
% incr. = percentage increase; not. = notched; unnot. = unnotched. phr.
|