High-Density Polyethylene and Heat-Treated Bamboo Fiber Composites: Nonisothermal Crystallization Properties
Table 1
Nonisothermal crystallization parameters of HDPE and its composites.
| Samples | (K/min) | (K) | (K) | (min) | (J·g−1) | (%) | (%) |
| HDPE | 2.5 | 397.9 | 396.7 | 1.141 | 122.0 | 44.2 | 45.2 | 5 | 397.3 | 396.7 | 0.652 | 126.8 | 45.9 | 10 | 396.3 | 395.0 | 0.411 | 121.1 | 43.9 | 20 | 395.5 | 393.7 | 0.263 | 122.5 | 44.4 | 35 | 394.2 | 392.2 | 0.194 | 116.8 | 42.3 |
| HDPE/heat-treated BF (373 K) | 2.5 | 398.1 | 397.1 | 1.033 | 84.4 | 51.0 | 49.9 | 5 | 397.4 | 396.4 | 0.585 | 80.6 | 48.6 | 10 | 396.5 | 395.4 | 0.378 | 78.1 | 47.1 | 20 | 395.5 | 393.8 | 0.253 | 75.2 | 45.4 | 35 | 394.6 | 392.6 | 0.192 | 73.6 | 44.5 |
| HDPE/heat-treated BF (423 K) | 2.5 | 398.1 | 397.1 | 1.007 | 81.9 | 49.5 | 49.4 | 5 | 397.4 | 396.4 | 0.596 | 79.4 | 48.0 | 10 | 396.5 | 395.4 | 0.373 | 76.7 | 46.3 | 20 | 395.5 | 393.9 | 0.253 | 73.6 | 44.4 | 35 | 394.3 | 391.9 | 0.207 | 67.9 | 41.0 |
| HDPE/heat-treated BF (453 K) | 2.5 | 398.1 | 397.2 | 1.210 | 83.2 | 50.0 | 51.5 | 5 | 397.3 | 396.4 | 0.657 | 78.7 | 47.5 | 10 | 396.6 | 395.4 | 0.368 | 74.0 | 44.7 | 20 | 395.5 | 395.3 | 0.262 | 70.8 | 42.7 | 35 | 394.7 | 392.7 | 0.183 | 70.1 | 42.3 |
|
|