High-Density Polyethylene and Heat-Treated Bamboo Fiber Composites: Nonisothermal Crystallization Properties
Table 2
Nonisothermal kinetic parameters at different relative crystallization of HDPE and its composites based on the Jeziorny model.
| Samples | /K/min | | | | | | |
| HDPE | 2.5 | 2.96 | 0.47 | 2.95 | 0.19 | 1.54 | 0.9999 | 5 | 3.1 | 1.42 | 26.23 | 0.28 | 1.92 | 0.9995 | 10 | 2.88 | 1.82 | 65.68 | 0.18 | 1.52 | 0.9999 | 20 | 2.74 | 2.31 | 202.19 | 0.12 | 1.30 | 0.9988 | 35 | 2.65 | 2.65 | 446.34 | 0.08 | 1.19 | 0.9982 |
| 373 K BF/HDPE | 2.5 | 3.05 | 0.67 | 4.65 | 0.27 | 1.85 | 0.9990 | 5 | 2.96 | 1.35 | 22.5 | 0.27 | 1.86 | 0.9992 | 10 | 2.89 | 1.94 | 87.54 | 0.19 | 1.56 | 0.9996 | 20 | 2.93 | 2.44 | 275.99 | 0.12 | 1.32 | 0.9993 | 35 | 2.98 | 2.9 | 795.39 | 0.08 | 1.21 | 0.9945 |
| 423 K BF/HDPE | 2.5 | 3.3 | 0.86 | 7.33 | 0.35 | 2.22 | 0.9996 | 5 | 2.8 | 1.16 | 14.53 | 0.23 | 1.71 | 0.9987 | 10 | 2.68 | 1.75 | 56.02 | 0.17 | 1.50 | 0.9973 | 20 | 2.68 | 2.11 | 128.54 | 0.11 | 1.27 | 0.9994 | 35 | 2.89 | 2.63 | 422.02 | 0.08 | 1.19 | 0.9995 |
| 453 K BF/HDPE | 2.5 | 2.56 | 0.4 | 2.49 | 0.16 | 1.44 | 0.9991 | 5 | 2.33 | 0.74 | 5.49 | 0.15 | 1.41 | 0.9964 | 10 | 3.38 | 2.44 | 273.11 | 0.24 | 1.75 | 0.9993 | 20 | 3.16 | 2.66 | 455.38 | 0.13 | 1.36 | 0.9990 | 35 | 2.96 | 2.96 | 911.61 | 0.08 | 1.21 | 0.9997 |
|
|