Research Article
Influence of Processing Conditions on the Thermal Stability and Mechanical Properties of PP/Silica-Lignin Composites
Table 2
Dispersive characteristic of pure precursors (silica and lignin) and silica-lignin hybrid fillers.
| Sample | Dispersive properties | Particle size distribution from Zetasizer Nano ZS (nm) | Particle diameter from Mastersizer 2000 (µm) | (0.1) | (0.5) | (0.9) |
| Syloid 244 + kraft lignin (1 : 1) | 106–295; 1990–5560 | 2.8 | 9.2 | 20.0 | Syloid 244 + kraft lignin (2 : 1) | 91–220; 1990–4800 | 2.7 | 9.0 | 19.9 | Syloid 244 + kraft lignin (5 : 1) | 79–122; 1720–4150 | 2.8 | 8.7 | 19.5 |
| Syloid 244 | 39–295; 1720–2670 | 2.0 | 7.2 | 18.1 | Kraft lignin | 1990–5560 | 5.0 | 12.5 | 38.6 |
|
|