Antibacterial Additive for Polystyrene Based on Silver Nanoparticles Supported on Titanium Dioxide

Waldo-Mendoza, Miguel A.; Martínez-Jothar, Lucía; Oros-Ruiz, Socorro; Villabona-Leal, E. G.; Céspedes-Covarrubias, Luis Manuel; Quiñones-Jurado, Zoe V.; Ortega, Eduardo; Pérez, Elías

doi:https://doi.org/10.1155/2016/1641352

International Journal of Polymer Science

On this page

Abstract Introduction Experimental Results and Discussion Conclusions Acknowledgments References Copyright Related Articles

Research Article | Open Access

Volume 2016 | Article ID 1641352 | https://doi.org/10.1155/2016/1641352

Antibacterial Additive for Polystyrene Based on Silver Nanoparticles Supported on Titanium Dioxide

Miguel A. Waldo-Mendoza,^1,2Lucía Martínez-Jothar,³Socorro Oros-Ruiz,⁴E. G. Villabona-Leal,³Luis Manuel Céspedes-Covarrubias,²Zoe V. Quiñones-Jurado,²Eduardo Ortega,⁵and Elías Pérez³

Academic Editor: Ing Kong

Received01 Jul 2016

Accepted20 Oct 2016

Published16 Nov 2016

Abstract

Silver nanoparticles supported on titanium dioxide nanoparticles (Ag/TiO₂) were incorporated and evaluated as antibacterial additive for polystyrene materials. These particles were synthesized using a deposition-precipitation method by adding silver nitrate as metallic precursor, sodium hydroxide as reducing agent, and commercial TiO₂ (P25) as support. Rectangular pieces of polystyrene (PS) containing 100, 300, 500, and 700 ppm (wt.%) of the additive were made using an extrusion-injection molding process, and they were evaluated for their antibacterial properties against Escherichia coli using the Pour Plate method. Particles were distributed on the PS surface, and PS pieces presented a good antibacterial efficiency at 100, 300, and 500 ppm and decreased for 700 ppm due to an additive agglomeration on the PS surface. These results validate the antibacterial properties of Ag/TiO₂, determine a concentration limit at which the additive is well distributed on the PS surface, and assess the importance of Ag in this system.

1. Introduction

Antimicrobials are natural or synthetic chemical compounds that kill or suppress the growth of viruses, bacteria, and/or fungi. Activity against bacteria and fungi is currently of major interest in the plastic industry as it promotes preservation and increased shelf life of the goods [1]. Polystyrene is an easily moldable material for injection, blown, extrusion, and thermoformed processes. It is also a material with wide applications in electrodomestics and food and pharmaceutical containers. These applications made polystyrene a suitable material to test the Ag/TiO₂ composite as an antimicrobial agent [2].

The use of silver based antimicrobials has dramatically increased in the plastic industry due mainly to low toxicity to humans as well as long-lasting efficacy. Silver (Ag) nanoparticles can be easily synthesized and incorporated into polymeric matrices, making it possible to use them as additives against bacterial action. The antibacterial activity of silver nanoparticles relies on several mechanisms, including damage to the cell wall, increase in the permeability and leakage of intracellular substances, alteration in the expression of envelope proteins and heat shock proteins, dissipation of the proton motive force, collapse of the plasma membrane potential, and decrease of intracellular ATP [3, 4]. Additionally, the liberation of silver ions increases the bactericidal effect since they are known to participate in the generation of reactive oxygen species, alter proteins by interacting with thiol groups, and induce DNA condensation leading to the loss of bacterial replication [5, 6].

On the other hand, titanium dioxide (TiO₂) is an additive currently used in the plastic industry that can also exhibit photocatalytic properties when it is exposed to UV radiation leading to the generation of electrons and holes that are able to oxidize water and hydroxide ions to produce highly reactive hydroxyl radicals capable of decomposing bacterial cell membranes [7]. These properties of TiO₂ can also be enhanced by the presence of silver nanoparticles on its surface (Ag/TiO₂). For instance, photocatalytic degradation of rhodamine B and 2,4,6-trichlorophenol was more effective using Ag/TiO₂ than TiO₂ alone, and TiO₂ films that contained silver exhibited a higher antibacterial activity against Escherichia coli than TiO₂ by itself [8–10]. The use of Ag/TiO₂ nanoparticles is presented in this work as a potential antibacterial additive given the properties of the individual components. They were obtained by simultaneous synthesis and deposition of Ag nanoparticles on the TiO₂ particle surface through a deposition-precipitation method, which allows for a controlled particle growth [11]. The materials generated by this method present higher photo oxidizing activities than those synthesized using other procedures (colloidal deposition, photodeposition, impregnation, etc.) [12, 13]. However, the size, shape, and metal concentration on the surface of the support are sensitive to parameters such as the pH of the reaction mixture [14–16]. For that reason, in this study we have synthesized Ag/TiO₂ varying the pH and keeping constant all other synthesis conditions. We have found that while nanoparticle size is not affected by pH variations, the presence of Ag on the TiO₂ surface is sensitive to this difference, being greater at pH 9. Ag/TiO₂ nanoparticles were then incorporated into PS through an extrusion-injection process, resulting in rectangular pieces containing 100, 300, 500, and 700 ppm (wt.) of Ag/TiO₂, with respect to the PS content. The PS containing this additive displays antibacterial properties against Escherichia coli even in the absence of light. As discussed, this property is directly related to the presence of the Ag/TiO₂ on the PS surface and also to the effectivity of the Ag in this additive.

2. Experimental

2.1. Silver Nanoparticles Synthesis and Deposition on

Ag/TiO₂ nanoparticles were synthesized in the absence of light through a deposition-precipitation method using silver nitrate (Fermont) as metallic precursor, sodium hydroxide (Caledon Laboratories LTD) as reducing agent, and TiO₂ Degussa P25 (Degussa Corporation/Pigments Group) as support. Briefly, an aqueous solution of silver nitrate containing 1.5 wt.% of silver on TiO₂ was added to an aqueous suspension of TiO₂. The mixture was heated to 80°C under vigorous stirring and the pH was adjusted to 9, 11, or 12 using sodium hydroxide. Heating and mixing were held for two hours, then the solution was centrifuged (10000 rpm), and the precipitate was washed with water at 50°C. After a second centrifugation, the solid was dried in an oven at 80°C for 12 hours, ground, and stored in the dark.

2.2. Nanoparticle Characterization

The size and shape of Ag/TiO₂ particles were characterized by a JEOL JEM-1230 TEM operated at 100 KV in the bright field imaging mode. Particle size and size distributions were calculated by measuring around 200 metal particles. SEM-EDX analysis was performed on a Philips FEI microscope model XL-30-PW6630/01 operated at 20 kW.

2.3. Extrusion of Polystyrene with

A mixture of Ag/TiO₂ and PS was injected using an Injection Molding Machine Battenfeld, Model LCMI in which the temperature of the barrel ranged between 190 and 210°C. The temperature of the mold was 27°C, the shoot volume was 43 cc, the screw speed was of 43 rpm, the pressure was 8.27 MPa, the cooling time was 15 s, and the cycle consisted of 31 s in total. This process resulted in the production of PS-Ag/TiO₂ rectangular pieces with dimensions of 100 × 70 × 3 mm, which contained 100, 300, 500, and 700 ppm (wt.) of Ag/TiO₂ with respect to the PS content.

2.4. Polystyrene- Surface Characterization

An Atomic Force Microscope (AFM) Multimode with a NanoScope IIIa controller (Veeco Metrology Group, Santa Barbara, USA) was used in intermittent contact mode using nonconductive silicon rectangular cantilevers (Bruker MPP-11120, tip radius ~8 nm) with a length of 125 μm and nominal frequency of 300 KHz to obtain images in phase contrast, which allowed the study of the dispersion of Ag/TiO₂ nanoparticles on the PS surface. The images were processed by using the NanoScope Analysis software (version 1.40, Bruker Corporation). The presence of the nanoparticles on the PS surface was confirmed by analyzing the phase histogram from the raw data matrix acquired. The percentage of the PS surface covered by Ag/TiO₂ was estimated as the ratio between the areas under the peaks observed in the phase distribution of the samples:where the subindexes PS and NP refer to the PS surface and the nanoparticles, respectively. Additionally, the dissipated energy during the tip-surface interaction can be calculated from the change in the oscillation amplitude and phase lag ϕ, using the equation:in which is the amplitude during testing, is the free amplitude, is the force constant of the cantilever, and is the quality factor [17]. This dissipative energy is used to distinguish different components on the material surface [18–20].

2.5. Antibacterial Activity of PS- Samples

Antibacterial tests, performed on Escherichia coli ATCC 25922, were conducted as follows: 400 μL of a bacterial suspension containing a total of 4 × 10⁵ colony forming units was placed at the center of the test surface that had been previously cut to a square with dimensions of 50 × 50 mm. The suspension on the PS surface was covered using a flexible film square (40 × 40 mm) and the sample was incubated in a chamber (relative humidity > 90%), in the dark, at °C for hours. It must be kept in mind that under this condition (incubation in the absence of light) it is unlikely that TiO₂ will exhibit antibacterial effect, since this is dependent on its photocatalytic properties. Therefore, antibacterial activity of the sample will only be attributed to the action of silver. After the incubation, the sample was placed on a plastic bag and 10 mL of Tryptic Soy Broth (Bioxon) was added and used to wash the sample in views to recover the bacteria present in it. The bacterial count was performed using the Pour Plate method: from the wash, dilutions ranging from 10⁻¹ to 10⁻¹⁰ were made in Phosphate Buffer Saline and 1 mL of each dilution was placed in a petri dish to which liquid Plate Count Agar (Bioxon) was added. The sample was homogenized and after the agar hardened it was incubated at °C for 48 hours. Counting was performed in plates containing between 30 and 300 colonies.

3. Results and Discussion

3.1. Characterization of Nanoparticles

The size of silver nanoparticles was obtained from the analysis of TEM images as presented in Figure 1. The silver nanoparticles synthesized at pH of 9, 11, and 12, using 1.5 wt.% of Ag/TiO₂, are presented in Figures 1(a), 1(b), and 1(c), respectively. The average Ag particle sizes obtained were nm, nm, and nm, respectively. All nanoparticles displayed approximately the same shape regardless of the pH, even though the influence of pH on nanoparticle assembly, size, and distribution was previously reported [21–23]; in our case for the different pH evaluated, it did not seem to have a determining effect on the particle size. The effect of metal loading of Ag on TiO₂ as confirmed by SEM-EDX analysis and scanning electron micrography is presented in Figure 2(a) where the following can be observed the presence of agglomerates of Ag/TiO₂ composites on the surface of the polymer and in Figure 2(b) the EDS analysis to determine metal loadings, showing that the effect of pH did not have a significant effect on the amount of silver deposited: , , and wt.%, respectively, for pH 9, pH 11, and pH 12.

(a)

(b)

(c)

(a)

(b)

3.2. AFM Characterization of PS- Samples

Figure 3 presents AFM height, phase contrast, and energy dissipation images (columns (a), (b), and (c), resp.) of a PS matrix containing 100, 300, 500, and 700 ppm of Ag/TiO₂, acquired within the month of its fabrication. These images showed distinctive local zones produced by the presence of nanoparticles at the surface of the material which contrasts with the reference sample that consists of pure PS. The presence of the nanoparticles on the PS surface is expected due to their difference in solubility: while PS is hydrophobic in nature and nanoparticles are hydrophilic, this difference induces the presence of Ag/TiO₂ on the PS surface. In addition, the temperatures used for the injection of PS and Ag/TiO₂ could facilitate the migration of the particles into the surface [24].

(a)

(b)

(c)

Figure 3 also highlights that the presence of agglomerates of the antibacterial additive reaches a maximum at a concentration of 700 ppm. This last result is not surprising since nanoparticles tend to agglomerate due to the large interparticle forces that exist between them (i.e., van der Waals forces) [25, 26].

The dispersion of these nanoparticles on the PS surface is corroborated by the analysis of the phase histograms shown in Figure 4. As observed, there are three histograms with a bimodal distribution (at 100, 300, and 700 ppm) and two with a unimodal distribution (at 0 and 500 ppm). The existence of two modes exhibits a poor distribution of the additive into the matrix surface, while the unimodal distribution coincides with the image from the PS alone and the image from the sample with the best nanoparticle distribution on the surface. In consequence, the nanoparticle dispersion on the PS surface was favored at low concentrations of Ag/TiO₂, with the most homogenous distribution of nanoparticles achieved at 500 ppm. In order to confirm the presence of the nanoparticles on the PS surface, the energy dissipation of the cantilever’s oscillation was calculated, to give the energy that we are losing each cycle of the tapping mode as that value will depend on the material, resulting in values between 29.2 and 44.0 aJ for the PS, in accordance with previous reports, and values between 8.8 and 21.4 aJ for the regions affected by the nanoparticles [20]. This reduction in energy is expected for the nanoparticles given that they dissipate less energy and therefore indicate the dispersion of a harder additive (Ag/TiO₂) into the surface of a softer (PS) matrix. This approach presents a nondestructive subsuperficial characterization technique that avoids heating, radiolysis, and degradation of the polymer matrix.

The percentage of surface coverage of the PS samples containing different amounts of Ag/TiO₂ was calculated from results presented in Figure 5, as described above. The values obtained were 54.7%, 52.3%, 89.3%, and 23.1% for the samples containing 100, 300, 500, and 700 ppm. These values, related to the surface coverage, are a clear indicator of the expected antibacterial effects of these composites.

3.3. Antibacterial Activity of PS- Samples

Antibacterial activity was evaluated through the inoculation of 4 × 10⁵ colony forming units of E. coli on the different PS plates containing Ag/TiO₂. The inoculation was followed by a hours of incubation. As shown in Figure 4, PS-Ag/TiO₂ pieces display different degrees of antibacterial activity compared to bare PS and said activity is directly related to the surface coverage of the PS samples with Ag/TiO₂. It is important to note that the PS test pieces inhibited bacterial growth by more than 80% at Ag/TiO₂ loadings of 100 ppm, 300 ppm, and 500 ppm. The antibacterial activity of Ag/TiO₂ nanoparticles on PS could be the result of one or several of the antibacterial mechanisms mentioned above (see Section 1). On the other hand, a severe decrease in the antibacterial activity was observed for Ag/TiO₂ 700 ppm, indicating that there is a concentration limit beyond which the antibacterial effect of this additive is diminished. This is evidently related to the Ag/TiO₂ agglomerates formed at 700 ppm, which reduce the contact surface between the antibacterial composite and E. coli resulting in less bacterial death than for the other concentrations in which the nanoparticles are more evenly distributed on the PS surface. Taking into consideration this information and the data obtained from the AFM images, it is evident that the antibacterial effect of Ag/TiO₂ is more likely a result of its distribution in the surface of the PS, rather than of its bulk concentration.

4. Conclusions

An antibacterial additive based on Ag/TiO₂ nanoparticles was evaluated and validated using PS as plastic matrix. Ag/TiO₂ nanoparticles were mixed with the PS through an extrusion-injection process and nanoparticles were localized on the PS surface, as shown by AFM characterization. Indeed, the antibacterial effect was directly correlated with the presence of the Ag/TiO₂ nanoparticles on the PS surface. The antibacterial tests against E. coli were carried at 100, 300, 500, and 700 ppm (wt) of Ag/TiO₂, with respect to the PS content, in the absence of light to assess the effect of Ag in the antibacterial additive. At low concentrations (100, 300, and 500 ppm), bacterial growth inhibition was greater than 80%, showing that Ag/TiO₂ has good antibacterial properties independently of the concentration values. However, agglomerates were observed at 700 ppm accompanied by a diminishing antibacterial effect. This finding established a limit for the additive concentration that can be used for the production of antibacterial PS surfaces. The previous result shows a promising approach for the development of a new family of antimicrobial additives for plastics. There is undoubtedly a trend toward the use of more environmental friendly antimicrobials with low toxicity. Antimicrobials based on silver substances meet this favorable toxicity profile and can be used at relatively low concentrations on the surface of plastic, showing important advantages over agents that cannot make similar claims.

Competing Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

Acknowledgments

The authors thank A. M. González-Amaro and M. L. Rivera-Martínez for their help and advice concerning the antibacterial activity tests. They also thank J. L. Menchaca (Universidad Autónoma de Nuevo León) for AFM facilities. This project was partially financed by A. Schulman de Mexico S. A. de C.V.

References

H. Zweifel, Plastic Additives Handbook, Hanser Gardner Publications, Munich, Germany, 2001.
S. Ebnesajjad and K. Modjarrad, Handbook of Polymer Applications in Medicine and Medical Devices, Elsevier, 2013.
I. Sondi and B. Salopek-Sondi, “Silver nanoparticles as antimicrobial agent: a case study on E. coli as a model for Gram-negative bacteria,” Journal of Colloid and Interface Science, vol. 275, no. 1, pp. 177–182, 2004.
View at: Publisher Site | Google Scholar
C.-N. Lok, C.-M. Ho, R. Chen et al., “Proteomic analysis of the mode of antibacterial action of silver nanoparticles,” Journal of Proteome Research, vol. 5, no. 4, pp. 916–924, 2006.
View at: Publisher Site | Google Scholar
H.-J. Park, J. Y. Kim, J. Kim et al., “Silver-ion-mediated reactive oxygen species generation affecting bactericidal activity,” Water Research, vol. 43, no. 4, pp. 1027–1032, 2009.
View at: Publisher Site | Google Scholar
Q. L. Feng, J. Wu, G. Q. Chen, F. Z. Cui, T. N. Kim, and J. O. Kim, “A mechanistic study of the antibacterial effect of silver ions on Escherichia coli and Staphylococcus aureus,” Journal of Biomedical Materials Research, vol. 52, no. 4, pp. 662–668, 2000.
View at: Publisher Site | Google Scholar
S.-Q. Sun, B. Sun, W. Zhang, and D. Wang, “Preparation and antibacterial activity of Ag-TiO₂ composite film by liquid phase deposition (LPD) method,” Bulletin of Materials Science, vol. 31, no. 1, pp. 61–66, 2008.
View at: Publisher Site | Google Scholar
H. M. Sung-Suh, J. R. Choi, H. J. Hah, S. M. Koo, and Y. C. Bae, “Comparison of Ag deposition effects on the photocatalytic activity of nanoparticulate TiO₂ under visible and UV light irradiation,” Journal of Photochemistry and Photobiology A: Chemistry, vol. 163, no. 1-2, pp. 37–44, 2004.
View at: Publisher Site | Google Scholar
S. Rengaraj and X. Z. Li, “Enhanced photocatalytic activity of TiO₂ by doping with Ag for degradation of 2,4,6-trichlorophenol in aqueous suspension,” Journal of Molecular Catalysis A: Chemical, vol. 243, no. 1, pp. 60–67, 2006.
View at: Publisher Site | Google Scholar
O. Akhavan, “Lasting antibacterial activities of Ag-TiO₂/Ag/a-TiO₂ nanocomposite thin film photocatalysts under solar light irradiation,” Journal of Colloid and Interface Science, vol. 336, no. 1, pp. 117–124, 2009.
View at: Publisher Site | Google Scholar
Z. V. Quiñones-Jurado, M. Á. Waldo-Mendoza, H. M. Aguilera-Bandin, E. G. Villabona-Leal, E. Cervantes-González, and E. Pérez, “Silver nanoparticles supported on TiO₂ and their antibacterial properties: effect of surface confinement and nonexistence of plasmon resonance,” Materials Sciences and Applications, vol. 5, no. 12, pp. 895–903, 2014.
View at: Publisher Site | Google Scholar
L. Prati and A. Villa, “The art of manufacturing gold catalysts,” Catalysts, vol. 2, no. 1, pp. 24–37, 2011.
View at: Publisher Site | Google Scholar
S. Oros-Ruiz, J. A. Pedraza-Avella, C. Guzmán et al., “Effect of gold particle size and deposition method on the photodegradation of 4-chlorophenol by Au/TiO₂,” Topics in Catalysis, vol. 54, no. 8-9, pp. 519–526, 2011.
View at: Publisher Site | Google Scholar
M. Haruta, “Size- and support-dependency in the catalysis of gold,” Catalysis Today, vol. 36, no. 1, pp. 153–166, 1997.
View at: Publisher Site | Google Scholar
R. Zanella, S. Giorgio, C. R. Henry, and C. Louis, “Alternative methods for the preparation of gold nanoparticles supported on TiO₂,” Journal of Physical Chemistry B, vol. 106, no. 31, pp. 7634–7642, 2002.
View at: Publisher Site | Google Scholar
K. R. Souza, A. F. F. de Lima, F. F. de Sousa, and L. G. Appel, “Preparing Au/ZnO by precipitation–deposition technique,” Applied Catalysis A: General, vol. 340, no. 1, pp. 133–139, 2008.
View at: Publisher Site | Google Scholar
N. F. Martínez and R. García, “Measuring phase shifts and energy dissipation with amplitude modulation atomic force microscopy,” Nanotechnology, vol. 17, no. 7, pp. S167–S172, 2006.
View at: Publisher Site | Google Scholar
R. Garcia, C. J. Gómez, N. F. Martinez, S. Patil, C. Dietz, and R. Magerle, “Identification of nanoscale dissipation processes by dynamic atomic force microscopy,” Physical Review Letters, vol. 97, no. 1, Article ID 016103, 2006.
View at: Publisher Site | Google Scholar
Y. H. Liu, D. Wang, K. Nakajima et al., “Characterization of nanoscale mechanical heterogeneity in a metallic glass by dynamic force microscopy,” Physical Review Letters, vol. 106, no. 12, Article ID 125504, 2011.
View at: Publisher Site | Google Scholar
D. Wang, X.-B. Liang, Y.-H. Liu, S. Fujinami, T. Nishi, and K. Nakajima, “Characterization of surface viscoelasticity and energy dissipation in a polymer film by atomic force microscopy,” Macromolecules, vol. 44, no. 21, pp. 8693–8697, 2011.
View at: Publisher Site | Google Scholar
P. K. Sahoo, S. S. Kalyan Kamal, T. J. Kumar, B. Sreedhar, A. K. Singh, and S. K. Srivastava, “Synthesis of silver nanoparticles using facile wet chemical route,” Defence Science Journal, vol. 59, no. 4, pp. 447–455, 2009.
View at: Publisher Site | Google Scholar
M. Kamali, S. A. A. Ghorashi, and M. A. Asadollahi, “Controllable synthesis of silver nanoparticles using citrate as complexing agent: characterization of nanoparticles and effect of pH on size and cristallinity,” Iranian Journal of Chemistry and Chemical Engineering, vol. 31, pp. 21–28, 2012.
View at: Google Scholar
M. Vanaja, S. Rajeshkumar, K. Paulkumar, G. Gnanajobitha, C. Malarkodi, and G. Annadurai, “Kinetic study on green synthesis of silver nanoparticles using Coleus aromaticus leaf extract,” Advances in Applied Science Research, vol. 4, pp. 50–55, 2013.
View at: Google Scholar
X. Xu, Z. Zhang, and W. Liu, “Fabrication of superhydrophobic surfaces with perfluorooctanoic acid modified TiO₂/polystyrene nanocomposites coating,” Colloids and Surfaces A: Physicochemical and Engineering Aspects, vol. 341, no. 1–3, pp. 21–26, 2009.
View at: Publisher Site | Google Scholar
T. P. Selvin, J. Kuruvilla, and T. Sabu, “Mechanical properties of titanium dioxide-filled polystyrene microcomposites,” Materials Letters, vol. 58, no. 3-4, pp. 281–289, 2004.
View at: Publisher Site | Google Scholar
A. Chandra, L.-S. Turng, S. Gong, D. C. Hall, D. F. Caulfield, and H. Yang, “Study of polystyrene/titanium dioxide nanocomposites via melt compounding for optical applications,” Polymer Composites, vol. 28, no. 2, pp. 241–250, 2007.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2016 Miguel A. Waldo-Mendoza et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

2596

Downloads

1478

Citations