Plasma Treatment of Agave Fiber Powder and Its Effect on the Mechanical and Thermal Properties of Composites Based on Polyethylene
Table 1
Mechanical properties of composites with pristine AFP at 5, 10, and 20 wt% (200 and 325 mesh).
| Composite | AFP (%) | Young’s modulus (MPa) | Stress at break (MPa) | Elongation at break (%) |
| LDPE | 0 | 129.9 ± 19.1 | 13.3 ± 0.3 | 453.4 ± 18.3 |
| NMF-5-M200 | 5 | 157.0 ± 21.4 | 10.6 ± 0.5 | 64.9 ± 8.7 | NMF-10-M200 | 10 | 173.9 ± 15.0 | 11.3 ± 0.1 | 46.1 ± 1.2 | NMF-20-M200 | 20 | 171.7 ± 10.9 | 10.4 ± 0.2 | 32.8 ± 9.2 |
| NMF-5-M325 | 5 | 167.7 ± 8.70 | 11.2 ± 0.4 | 72.8 ± 4.0 | NMF-10-M325 | 10 | 185.0 ± 15.0 | 11.8 ± 0.1 | 42.4 ± 7.4 | NMF-20-M325 | 20 | 231.8 ± 6.30 | 12.7 ± 0.4 | 18.6 ± 4.0 |
|
|