Preparation and Characterization of a Bioartificial Polymeric Material: Bilayer of Cellulose Acetate-PVA
Table 5
Mechanical properties for the prepared material.
| Sample | Young’s modulus (MPa) | Tensile strength (MPa) | Elongation at break (%) | Thickness (mm) |
| CA | 1,832 ± 71 | 38 ± 4 | 7 ± 3 | 0.253 ± 0.01 | CA + ADD | 660 ± 87 | 13 ± 2 | 10 ± 2 | 0.311 ± 0.03 | PVA | 1,174 ± 189 | 16 ± 6 | 69 ± 15 | 0.128 ± 0.04 | PVA + ADD | 49 ± 6 | 18 ± 3 | 217 ± 25 | 0.094 ± 0.01 | Bilayer | 590 ± 53 | 11 ± 3 | 13 ± 4 | 0.340 ± 0.02 |
|
|