Effect of Modification with Various Epoxide Compounds on Mechanical, Thermal, and Coating Properties of Epoxy Resin
Table 4
Effect of modifier type and amount on mechanical properties.
| Modifier (wt.%) | Elongation at break (%) | Tensile strength (MPa) | -modulus (GPa) | Hardness (Shore D) |
| For neat ER | — | 0.487 | 41.75 | 5.59 | 75.5 |
| For M-ER with EMP | 10 | 0.542 | 59 | 6.50 | 83.9 | 20 | 0.545 | 58 | 5.53 | 81.0 | 30 | 0.556 | 56 | 4.97 | 81.5 | 40 | 0.559 | 56 | 4.80 | 73.0 |
| For M-ER with PhEP | 10 | 0.351 | 48 | 5.07 | 81.5 | 20 | 0.445 | 44 | 5.33 | 80.7 | 30 | 0.451 | 47 | 6.04 | 80.3 | 40 | 0.464 | 30 | 4.07 | 77.2 |
| For M-ER with CEH | 10 | 0.477 | 48 | 5.52 | 86.6 | 20 | 0.522 | 56 | 5.93 | 86.7 | 30 | 0.527 | 55 | 4.23 | 86.2 | 40 | 0.541 | 53 | 4.83 | 86.1 |
| For M-ER with FAGE | 10 | 0.532 | 51 | 4.37 | 79.7 | 20 | 0.540 | 49 | 4.93 | 80.2 | 30 | 0.527 | 50 | 5.73 | 78.2 | 40 | 0.536 | 39 | 4.83 | 72 |
|
|