International Journal of Polymer Science / 2016 / Article / Tab 1 / Research Article
Effect of Die Head Temperature at Compounding Stage on the Degradation of Linear Low Density Polyethylene/Plastic Film Waste Blends after Accelerated Weathering Table 1 Control samples (no exposure) colour parameters.
Materials (wt/wt%), DHT = 175°C V (100 LLDPE/0 waste) 29.0 −0.40 −3.5 B1 (90 LLDPE/10 waste) 26.0 −0.80 −4.53 B2 (75 LLDPE/25 waste) 25.2 −0.40 −4.8 B3 (50 LLDPE/50 waste) 23.0 −0.60 −5.9 B4 (25 LLDPE/75 waste) 20.1 −0.50 −5.6 B5 (10 LLDPE/90 waste) 18.0 −0.40 −5.5 Materials (wt/wt%), DHT = 185°C V (100 LLDPE/0 waste) 27.0 −0.12 −3.68 B1 (90 LLDPE/10 waste) 25.3 −0.58 −4.42 B2 (75 LLDPE/25 waste) 25.2 −0.51 −4.81 B3 (50 LLDPE/50 waste) 24.29 −0.47 −5.47 B4 (25 LLDPE/75 waste) 21.6 −0.47 −5.49 B5 (10 LLDPE/90 waste) 17.97 −0.36 −5.7 Materials (wt/wt%), DHT = 195°C V (100 LLDPE/0 waste) 27.6 −0.40 −3.95 B1 (90 LLDPE/10 waste) 6.9 −0.60 −4.24 B2 (75 LLDPE/25 waste) 24.8 −0.41 −5.01 B3 (50 LLDPE/50 waste) 23.6 −8.10 −5.52 B4 (25 LLDPE/75 waste) 21.0 −0.41 −5.70 B5 (10 LLDPE/90 waste) 16.9 −0.31 −5.44