In Situ Wire Drawing of Phosphate Glass in Polymer Matrices for Material Extrusion 3D Printing
Table 3
Tensile rest results for ABS:SEBS-g-MA loaded with P-glass at various weight percentages.
| Material | UTS (MPa) | ST. DEV | % EL at break | ST. DEV | Sample size () |
| ABS:SEBS-g-MA, P-glass 5% @240C | 14.8 | 0.2 | 69 | 4 | 4 | ABS:SEBS-g-MA, P-glass 10% @240C | 14.1 | 1.3 | 49 | 8 | 5 | ABS:SEBS-g-MA, P-glass 20% @240C | 11.0 | 0.5 | 63 | 14 | 5 | ABS:SEBS-g-MA, baseline @240C | 14.4 | 0.2 | 54 | 14 | 3 |
|
|