Effect of Quinacridone Pigments on Properties and Morphology of Injection Molded Isotactic Polypropylene
Table 3
Mechanical properties of isotactic polypropylene modified with quinacridone pigments.
| Sample | Tensile strength | Young modulus | Elongation at break | Impact strength | (MPa) | (MPa) | (%) | (kJ/m2) |
| Polypropylene (iPP) | | | | |
| iPP -quinacridone (ER 02) |
| 0.01 wt% | 32.2 ± 0.4 | 1332 ± 40 | 199 ± 30 | 39.7 ± 6.3 | 0.05 wt% | 33.1 ± 0.3 | 1423 ± 49 | 175 ± 33 | 43.1 ± 2.5 | 0.1 wt% | 33.4 ± 0.2 | 1376 ± 44 | 155 ± 40 | 31.2 ± 7.8 | 0.5 wt% | 34.1 ± 0.1 | 1421 ± 39 | 113 ± 41 | 28.3 ± 3.2 | 1 wt% | 34.2 ± 0.2 | 1411 ± 32 | 83 ± 24 | 24.5 ± 2.5 | 2 wt% | 33.6 ± 0.2 | 1378 ± 18 | 44 ± 7 | 15.9 ± 4.5 |
| iPP -quinacridone (E5B) |
| 0.01 wt% | 31.5 ± 0.6 | 1284 ± 82 | 197 ± 61 | 45.5 ± 4.8 | 0.05 wt% | 32.1 ± 0.2 | 1308 ± 73 | 164 ± 42 | 37.8 ± 7.9 | 0.1 wt% | 32.3 ± 0.2 | 1317 ± 66 | 144 ± 36 | 38.4 ± 4.7 | 0.5 wt% | 33.1 ± 0.2 | 1373 ± 83 | 99 ± 24 | 24 ± 2.5 | 1 wt% | 33.1 ± 0.3 | 1357 ± 104 | 49 ± 25 | 20.7 ± 3.2 | 2 wt% | 32.9 ± 0.2 | 1364 ± 68 | 26 ± 5 | 16.6 ± 1.1 |
|
|