A New Route to Fabricate Multifunctional and Multistage Composite Nanoparticle
Table 1
Fabrication condition and characterizations of gelatin-encapsulated nanoparticles.
| Entry | Preparative parameters | Characterization | PVA conc. (, %) | Water/oil ratio of the first emulsion | Diameter (nm, SEM) | Hydrodynamic diameter (DLS) | Zeta potential (mV) | Encapsulation efficiency (%) | Eff. diam. (nm) | PDI |
| Nano1 | 1 | 1 : 5 | 324 ± 180 | 313 | 0.091 | −10.7 ± 4.6 | 1.8 ± 0.3 | Nano2 | 3 | 1 : 5 | 194 ± 60 | 253 | 0.150 | −12.1 ± 7.3 | 1.1 ± 0.1 | Nano3 | 5 | 1 : 5 | 98 ± 14 | 191 | 0.092 | −9.3 ± 11.5 | 1.4 ± 0.4 | Nano4 | 3 | 1:10 | 179 ± 58 | 266 | 0.111 | −14.0 ± 9.4 | 1.1 ± 0.1 | Nano5 | 3 | 1 : 20 | 150 ± 63 | 267 | 0.227 | −12.0 ± 8.1 | 1.0 ± 0.1 |
|
|