Experimental Study on Unconfined Compressive Strength of Organic Polymer Reinforced Sand
Table 3
Results of density 1.4 g/cm3 samples with different PSS concentration and curing time.
| Serial number | PSS concentration (%) | Dry density (g/cm3) | Relative density (%) | Curing time (hour) | Peak strength (KPa) | Residual strength (KPa) | Strength of axial strain 15% (KPa) | Axial strain of failure (%) | Elasticity modulus (MPa) | Failure modulus (MPa) |
| S1 | water | 1.4 | 21.05 | / | / | / | / | / | / | / | S4 | 10 | 1.4 | 21.05 | 6 | 17.79 | 9.61 | 15.38 | 7.92 | 0.479 | 0.225 | S5 | 20 | 1.4 | 21.05 | 6 | 31.16 | 14.11 | 19.96 | 7.86 | 1.121 | 0.396 | S6 | 30 | 1.4 | 21.05 | 6 | 42.52 | 16.45 | 20.79 | 4.80 | 1.264 | 0.885 | S7 | 40 | 1.4 | 21.05 | 6 | 61.55 | 20.62 | 21.65 | 4.26 | 1.853 | 1.444 | S8 | 50 | 1.4 | 21.05 | 6 | 88.89 | 21.98 | 27.74 | 4.18 | 2.326 | 2.125 |
| S9 | 10 | 1.4 | 21.05 | 12 | 29.89 | 12.25 | 19.70 | 8.76 | 0.483 | 0.341 | S10 | 20 | 1.4 | 21.05 | 12 | 36.81 | 17.48 | 28.00 | 7.91 | 1.256 | 0.465 | S11 | 30 | 1.4 | 21.05 | 12 | 65.86 | 22.17 | 46.90 | 7.33 | 2.012 | 0.899 | S12 | 40 | 1.4 | 21.05 | 12 | 104.70 | 32.25 | 64.95 | 6.73 | 2.917 | 1.555 | S13 | 50 | 1.4 | 21.05 | 12 | 127.08 | 33.93 | 80.60 | 5.84 | 3.756 | 2.176 |
| S14 | 10 | 1.4 | 21.05 | 24 | 36.22 | 18.76 | 23.19 | 10.27 | 0.722 | 0.353 | S15 | 20 | 1.4 | 21.05 | 24 | 57.08 | 21.89 | 47.71 | 10.18 | 1.310 | 0.561 | S16 | 30 | 1.4 | 21.05 | 24 | 87.24 | 35.89 | 70.61 | 7.65 | 2.144 | 1.140 | S17 | 40 | 1.4 | 21.05 | 24 | 129.03 | 56.77 | 87.96 | 6.85 | 2.943 | 1.884 | S18 | 50 | 1.4 | 21.05 | 24 | 196.62 | 86.11 | 130.47 | 5.89 | 3.757 | 3.340 |
| S19 | 10 | 1.4 | 21.05 | 48 | 62.34 | 19.46 | 56.75 | 10.88 | 1.244 | 0.573 | S20 | 20 | 1.4 | 21.05 | 48 | 120.83 | 22.52 | 107.44 | 10.75 | 2.594 | 1.124 | S21 | 30 | 1.4 | 21.05 | 48 | 169.22 | 56.95 | 152.29 | 10.11 | 5.629 | 1.674 | S22 | 40 | 1.4 | 21.05 | 48 | 201.94 | 75.29 | 168.24 | 8.87 | 8.526 | 2.277 | S23 | 50 | 1.4 | 21.05 | 48 | 245.28 | 97.73 | 187.46 | 7.08 | 11.494 | 3.464 |
| S24 | 10 | 1.4 | 21.05 | 72 | 67.85 | 20.39 | 60.23 | 10.92 | 1.251 | 0.621 | S25 | 20 | 1.4 | 21.05 | 72 | 121.67 | 22.57 | 113.43 | 10.76 | 2.605 | 1.131 | S26 | 30 | 1.4 | 21.05 | 72 | 172.93 | 57.94 | 153.02 | 10.14 | 5.707 | 1.706 | S27 | 40 | 1.4 | 21.05 | 72 | 207.55 | 75.01 | 168.49 | 9.02 | 8.969 | 2.297 | S28 | 50 | 1.4 | 21.05 | 72 | 249.18 | 100.85 | 193.31 | 7.31 | 11.352 | 3.391 |
|
|