Research Article
Engineered Multifunctional Fluorinated Film Based on Semicontinuous Emulsion Polymerization Using Polymerizable Quaternary Ammonium Emulsifiers
Table 2
Influence of the nine stable pre-emulsions on the prepared emulsion properties.
| Sample | Conversion (%) | (theory) | (test) | Coagulum (%) | Viscosity (mPa⋅s) | Particle size (nm) | PDI | Freeze/thaw stability | Electrolyte stability | Storage stability |
| L1 | 95.22 | 11.99 | 11.19 | 0.108 | 17.5 | 189.4 | 0.037 | Pass | Pass | No change | L4 | 93.76 | 11.99 | 10.26 | 0.130 | 20.0 | 195.8 | 0.03 | Pass | Pass | No change | L6 | 94.16 | 11.99 | 10.67 | 0.135 | 35 | 130.1 | 0.021 | Pass | Pass | No change | L7 | 94.92 | 11.99 | 10.29 | 0.187 | 150 | 53.6 | 0.147 | Pass | Pass | Demix | L8 | 86.85 | 11.99 | 9.37 | 8.925 | 173 | 66.4 | 0.17 | Pass | Fail | Demix | L9 | 96.13 | 11.99 | 11.40 | 0.177 | 27.5 | 142.9 | 0.023 | Pass | Pass | No change | L10 | 88.25 | 12.34 | 9.88 | 9.238 | 370 | 87.1 | 0.191 | Pass | Pass | No change | L11 | 99.34 | 12.34 | 12.01 | 0.010 | 15.5 | 179.5 | 0.042 | Pass | Pass | No change |
|
|