New Solvent for Polyamide 66 and Its Use for Preparing a Single-Polymer Composite-Coated Fabric
Table 2
Values for the pH and the relative components and also the observations.
| Sample name | pH | U/Ca | U/FA | 100∗U/(FA + Ca + W) | 100∗Ca/(FA + U + W) | Observation∗ |
| 100-0-0-0 | −1.74 | — | 0.00 | 0.00 | 0.00 | Excellent | 60-7-20-13 | −0.74 | 0.33 | 0.11 | 7.14 | 25.00 | Excellent+ | 64-7-14-14 | −0.54 | 0.50 | 0.11 | 7.69 | 16.67 | Excellent | 90-0-0-10 | −1.10 | — | 0.00 | 0.00 | 0.00 | Excellent | 90-10-0-0 | −0.18 | — | 0.11 | 11.11 | 0.00 | Excellent | 82-9-9-0 | −0.75 | 1.00 | 0.11 | 10.00 | 10.00 | Excellent | 69-8-15-8 | −0.74 | 0.50 | 0.11 | 8.33 | 18.18 | Good | 67-4-30-0 | −1.64 | 0.13 | 0.06 | 3.85 | 42.11 | Good | 82-0-0-18 | −0.56 | — | 0.00 | 0.00 | 0.00 | Good | 75-8-17-0 | −0.95 | 0.50 | 0.11 | 9.09 | 20.00 | Good | 75-0-0-25 | −0.30 | — | 0.00 | 0.00 | 0.00 | Fairly good | 55-6-39-0 | −1.69 | 0.15 | 0.11 | 6.45 | 65.00 | Fairly poor | 50-8-42-0 | −1.61 | 0.20 | 0.17 | 9.09 | 71.43 | Fairly poor | 47-8-39-5 | −1.50 | 0.20 | 0.17 | 8.57 | 65.22 | Fairly poor | 56-6-25-13 | −0.91 | 0.25 | 0.11 | 6.67 | 33.33 | Poor | 50-6-28-17 | −0.90 | 0.20 | 0.11 | 5.88 | 38.46 | Poor | 43-7-36-14 | −1.08 | 0.20 | 0.17 | 7.69 | 55.56 | Bad | 38-6-43-13 | −1.42 | 0.15 | 0.17 | 6.82 | 74.07 | Bad | 35-6-48-12 | −1.66 | 0.12 | 0.17 | 6.12 | 92.59 | Bad |
|
|
The markings were assigned based on the homogeneity of the solutions and the uniformity of the cast film on the glass. |