Fatigue Fracture Properties and Morphology of Polyoxymethylene (POM) Plates Produced under Moderate Processing Conditions
Table 7
WAXD measurements of the CT specimens analyzed for the contribution of the different diffraction peaks to the total crystallinity.
| CT specimens | Crystallinity1 (%) | (100)2 (%) | (105)2 (%) | (115)2 (%) | (205)2 (%) | Amorphous fraction2 (%) |
| Delrin_CM | 75.8 ± 0.8 | 60.1 | 12.2 | 2.9 | 0.6 | 24.2 | Delrin_IM_60°C-MT | 72.6 ± 1.0 | 60.4 | 10.6 | 1.4 | 0.1 | 27.4 | Delrin_IM_90°C-MT_Pos1 | 75.1 ± 0.9 | 62.0 | 11.2 | 1.7 | 0.2 | 24.9 | Delrin_IM_90°C-MT_Pos2 | 75.9 ± 0.7 | 64.1 | 10.2 | 1.5 | 0.2 | 24.1 | Delrin_IM_110°C-MT | 74.3 ± 0.3 | 61.2 | 11.4 | 1.6 | 0.2 | 25.7 |
| Tenac_CM | 74.8 ± 0.5 | 58.6 | 12.6 | 3.0 | 0.7 | 25.2 | Tenac_IM_60°C-MT | 70.7 ± 0.7 | 57.0 | 11.8 | 1.7 | 0.2 | 29.3 | Tenac_IM_90°C-MT_Pos1 | 70.5 ± 0.8 | 56.4 | 12.1 | 1.7 | 0.3 | 29.5 | Tenac_IM_90°C-MT_Pos2 | 71.6 ± 0.6 | 58.0 | 11.7 | 1.7 | 0.2 | 28.4 | Tenac_IM_110°C-MT | 71.3 ± 0.4 | 56.9 | 12.3 | 1.8 | 0.3 | 28.7 |
|
|
1Average value ± standard deviation. 2Average value.
|