A Comparison Study of Antiultraviolet and Sustained Release Properties of Polydopamine/Avermectin Microcapsule and Microsphere
Table 4
Fitting results for release curves of AVM/PDAMS and AVM@PDAMC.
| Release model | pH | AVM@PDAMC | AVM/PDAMS | K1 | K2 | K3 | R2 | K1 | K2 | K3 | R2 |
| Zero-order model | 3 | 0.0042 | — | — | 0.9635 | 0.0053 | — | — | 0.7433 | 7 | 0.0024 | — | — | 0.9148 | 0.0035 | — | — | 0.8898 | 9 | 0.0031 | — | — | 0.8918 | 0.0040 | — | — | 0.8734 | First-order model | 3 | 0.0227 | 0.6857 | — | 0.8667 | 0.0639 | 0.8870 | — | 0.9279 | 7 | 0.0485 | 0.3953 | — | 0.7429 | 0.0498 | 0.5726 | — | 0.7971 | 9 | 0.0455 | 0.4932 | — | 0.8321 | 0.0438 | 0.6307 | — | 0.8765 | Hixson–Crowell model | 3 | 0.0023 | 0.5963 | — | 0.9027 | 0.0020 | 0.7593 | — | 0.6685 | 7 | 0.0016 | 0.5662 | — | 0.8586 | 0.0018 | 0.6413 | — | 0.8275 | 9 | 0.0018 | 0.5994 | — | 0.8297 | 0.0020 | 0.6430 | — | 0.8064 | Weibull model | 3 | 15.7661 | 0.5727 | — | 0.9538 | 6.2909 | 0.5922 | — | 0.9951 | 7 | 10.8111 | 0.3710 | — | 0.9825 | 7.8666 | 0.4169 | — | 0.9861 | 9 | 10.0934 | 0.4199 | — | 0.9886 | 9.1389 | 0.4799 | — | 0.9930 | Higuchi model | 3 | 0.0606 | — | — | 0.9666 | 0.1005 | — | — | 0.7808 | 7 | 0.0432 | — | — | 0.8259 | 0.0627 | — | — | 0.8367 | 9 | 0.0530 | — | — | 0.8813 | 0.0671 | — | — | 0.9119 | Baker–Lonsdale model | 3 | 8.7246 × 10−4 | — | — | 0.9935 | 0.0030 | — | — | 0.9811 | 7 | 3.4348 × 10−4 | — | — | 0.9840 | 8.2042 × 10−4 | — | — | 0.9866 | 9 | 5.5707 × 10−4 | — | — | 0.9871 | 0.0010 | — | — | 0.9919 | Korsmeyer–Peppas model | 3 | 0.4392 | 0.0785 | — | 0.9750 | 0.3072 | 0.2269 | — | 0.9717 | 7 | 0.3154 | 0.0941 | — | 0.9898 | 0.3184 | 0.1350 | — | 0.9950 | 9 | 0.3380 | 0.1051 | — | 0.9938 | 0.3539 | 0.1247 | — | 0.9967 | Quadratic model | 3 | −4.5900 × 10−7 | 1.1162 × 10−4 | — | 0.8162 | −1.1684 × 10−6 | 2.2483 × 10−4 | — | 0.5998 | 7 | −4.1335 × 10−7 | 8.7622 × 10−5 | — | 0.4807 | −6.2282 × 10−7 | 1.2960 × 10−4 | — | 0.5316 | 9 | −5.0533 × 10−7 | 1.0750 × 10−4 | — | 0.6004 | −6.4022 × 10−7 | 1.3630 × 10−4 | — | 0.6741 | Logistic model | 3 | 38.0052 | 0.0329 | 0.7066 | 0.9934 | 13.4592 | 0.0772 | 0.9055 | 0.9679 | 7 | 22.0411 | 0.0354 | 0.4440 | 0.9693 | 19.5788 | 0.0419 | 0.6222 | 0.9699 | 9 | 20.9608 | 0.0430 | 0.5287 | 0.9594 | 21.3379 | 0.0467 | 0.6653 | 0.9502 |
|
|