Investigation of the Thermo-Mechanical Properties of Blend Films Based on Hemicelluloses and Cellulose
Table 3
Tensile testing results of the blend films.
| Sample | Tensile strength (MPa) | Tensile strain at break (%) | Young’s modulus (GPa) | Thickness (μm) |
| QH | 18.02 ± 2.01 | 1.30 ± 0.50 | 1.30 ± 0.02 | 80 ± 2 | CMC | 116.04 ± 10.00 | 17.2 ± 1.21 | 2.03 ± 0.01 | 50 ± 8 | PE | 11.21 ± 1.30 | 42.1 ± 0.90 | 0.03 ± 0.03 | 10 ± 2 | Film 1 | 55.02 ± 0.61 | 3.9 ± 0.90 | 1.54 ± 0.43 | 57 ± 2 | Film 2 | 65.21 ± 5.23 | 4.3 ± 0.70 | 1.60 ± 0.40 | 50 ± 4 | Film 3 | 54.22 ± 7.90 | 3.4 ± 0.10 | 1.59 ± 0.18 | 46 ± 3 |
|
|