Fully Biobased Aliphatic Anionic Oligoesters: Synthesis and Properties
Table 3
Thermal properties of biobased oligoesters.
Sample
Td(5%) (°C)a
RW (%)b
Tg (°C)c
Tm (°C)d
∆Hm (J.g-1)e
∆Hr (J.g-1)f
PBSu100Ss0
277
2.7
−38
114
111
68
PBSu80Ss20
268
16.3
−33
99
45
—
PBSu70Ss30
263
17.8
−29
—
—
—
PBSu60Ss40
260
24.2
−24
—
—
—
cPBSu70Ss30
—
—
53
—
—
—
PBC18100Ss0
360
1.15
−68
18
51
42
PBC1890Ss10
312
5
−66
17
37
31
PBC1880Ss20
298
10.8
−64
8
15
22
PBC1870Ss30
289
10
−63
6
9
15
PBDA100Ss0
384
0.5
−56
—
—
—
PBDA90Ss10
353
2.1
−55
—
—
—
PBDA80Ss20
335
3.3
−54
—
—
—
PBDA70Ss30
288
6.9
−55
—
—
—
PBISu100Ss0
308
4
−7
—
—
—
PBISu90Ss10
286
13
−2
—
—
—
PBISu80Ss20
269
16
9
—
—
—
PBISu70Ss30
227
24
12
—
—
—
aDegradation temperature at which a 5% weight loss was observed in TGA. bRemaining weight at 500°C. cGlass transition temperature taken as the inflection point of the DSC traces. dMelting temperatures were registered by DSC. eMelting enthalpies were registered by DSC. fCrystallization enthalpies were registered by DSC.