Thermal Stability and Flame Resistance of the Coextruded Wood-Plastic Composites Containing Talc-Filled Plastic Shells
| Name | (°C) | WLo (%) | (°C) | WLp (%) | (°C) | WLs (%) | Residue (%) | (°C) | (%) |
| AD60 | 459.0 | 30.13 | 470.5 | 65.74 | 480.4 | 95.42 | 0.83 | 21.4 | 65.29 | Colorant | 446.3 | 15.83 | 458.2 | 26.70 | 674.9 | 44.75 | 52.23 | 228.6 | 28.92 | Talc | 529.2 | 5.49 | 560.7 | 13.05 | 625.2 | 18.78 | 80.91 | 96 | 13.29 | B | 462.2 | 35.31 | 469.6 | 58.63 | 480.9 | 89.08 | 5.93 | 18.7 | 53.77 | C | 456.5 | 20.85 | 468.9 | 51.60 | 483.2 | 84.44 | 11.97 | 26.7 | 63.59 | D | 461.0 | 26.01 | 470.0 | 50.43 | 480.6 | 78.36 | 13.58 | 19.6 | 52.35 | E | 460.2 | 22.24 | 471.5 | 48.06 | 663.8 | 76.36 | 23.48 | 203.6 | 54.12 | F | 460.5 | 19.21 | 472.0 | 42.73 | 675.6 | 68.95 | 30.93 | 215.1 | 49.74 | G | 459.8 | 14.84 | 470.7 | 32.60 | 684.7 | 56.70 | 43.17 | 136.7 | 41.86 | Core | 341.3 | 0.18 | 465.4 | 71.72 | 478.0 | 82.56 | 12.76 | 136.7 | 82.38 |
|
|