Analysis of Terpolymerization Systems for the Development of Carbon Fiber Precursors of PAN
Table 4
Layout and results of L12 experimental design of the terpolymerization systems.
| Test | Code | Controllable factors | Conv (%) | (g/mol) | Es | A | B | C | D | E | F | G | H | I |
| 1 | TPAN-1 | 50 | 0.01 | 3 | 5 | 1 | VA | IA | 1 | 250 | 17 | | 4.0 | 2 | TPAN-2 | 50 | 0.01 | 3 | 5 | 1 | MA | BA | 2 | 350 | 36 | | 1.0 | 3 | TPAN-3 | 50 | 0.01 | 5 | 10 | 3 | VA | IA | 1 | 350 | 12 | | 4.6 | 4 | TPAN-4 | 50 | 0.02 | 3 | 10 | 3 | VA | BA | 2 | 250 | 44 | | 1.2 | 5 | TPAN-5 | 50 | 0.02 | 5 | 5 | 3 | MA | IA | 2 | 350 | 31 | | 4.3 | 6 | TPAN-6 | 50 | 0.02 | 5 | 10 | 1 | MA | BA | 1 | 250 | 30 | | 0.7 | 7 | TPAN-7 | 60 | 0.01 | 5 | 10 | 1 | VA | BA | 2 | 350 | 32 | | 1.8 | 8 | TPAN-8 | 60 | 0.01 | 5 | 5 | 3 | MA | BA | 1 | 250 | 28 | | 1.6 | 9 | TPAN-9 | 60 | 0.01 | 3 | 10 | 3 | MA | IA | 2 | 250 | 41 | | 4.7 | 10 | TPAN-10 | 60 | 0.02 | 5 | 5 | 1 | VA | IA | 2 | 250 | 34 | | 4.2 | 11 | TPAN-11 | 60 | 0.02 | 3 | 10 | 1 | MA | IA | 1 | 350 | 48 | | 1.6 | 12 | TPAN-12 | 60 | 0.02 | 3 | 5 | 3 | VA | BA | 1 | 350 | 53 | | 1.3 |
|
|
Conversion rate ( Conv); average viscosimetric molecular weight ( ); and extent of stabilization ( Es) of TPAN developed by solution terpolymerizations. |