Analysis of Terpolymerization Systems for the Development of Carbon Fiber Precursors of PAN
Table 5
ANOVA results for the experimental design used in terpolymerization systems.
| Variable | Conv | | Es | -ratio () | value () | -ratio () | value () | -ratio () | value () |
| A | 30.22 | 0.032 | 0.79 | 0.469 | 0.08 | 0.805 | B | 37.81 | 0.025 | 15.36 | 0.059 | 3.85 | 0.189 | C | 39.29 | 0.025 | 634.49 | 0.002 | 2.59 | 0.249 | D | 0.51 | 0.549 | 0.08 | 0.806 | 0.72 | 0.486 | E | 0.89 | 0.445 | 82.70 | 0.012 | 4.36 | 0.172 | F | 3.27 | 0.212 | 12.79 | 0.070 | 2.36 | 0.264 | G | 10.81 | 0.081 | 135.87 | 0.007 | 53.58 | 0.018 | H | 7.28 | 0.114 | 97.52 | 0.010 | 2.31 | 0.268 | I | 0.15 | 0.735 | 0.01 | 0.921 | 0.83 | 0.460 |
|
|
Conversion rate ( Conv); average viscosimetric molecular weight ( ); and extent of stabilization ( Es) of TPAN developed by solution terpolymerization. |