Inhibitor | Concentration | Material | Test conditions | Maximum efficiency | Test technique | References |
|
HCl-doped poly(o-ethoxy aniline) | 200 ppm | Pure Fe | 1 M HCl, RT | 92% | LPR | [150] |
Sulfamic acid-doped poly(o-ethoxy aniline) | 75 ppm | Pure Fe | 1 M HCl, RT | 93% | WL | [150] |
HCl-doped poly(o-methoxy aniline) | 200 ppm | Pure Fe | 1 M HCl, RT | 91% | LPR | [151] |
Sulfamic acid-doped poly(o-methoxy aniline) | 75 ppm | Pure Fe | 1 M HCl, RT | 92% | LPR | [151] |
Poly(styrene sulfonic acid)-doped PANI | 70 ppm | MSteel | 1 M HCl, 30°C | 85% | Tafel | [152] |
Low-MW poly(o-ethoxyaniline) | 100 ppm | CSteel | 1 M HCl, 60°C | 96% | Tafel | [153] |
Self-doped polyanthranilic acid | 60 ppm | MSteel | 0.5 M HCl, 60°C | 94% | EIS | [154] |
PANI and PDDMAC blend | 150 ppm | Pure Fe | 1 M HCl, RT | 59% | Tafel | [155] |
Poly(aniline-co-2-isopropylanilne) | 80 ppm | Pure Fe | 1 M HCl, RT | 72% | Tafel | [156] |
LiSIPA-doped poly(aniline-co-2-isopropylaniline) | 80 ppm | Pure Fe | 1 M HCl, RT | 72% | Tafel | [157] |
Poly(aniline-formaldehyde) | 10 ppm | MSteel | 1 M HCl, 35 °C | 98% | WL | [158] |
Poly(vinyl alcohol-o-methoxy aniline) composite | 2000 ppm | MSteel | 1 M HCl, RT | 91% | EIS | [159] |
Poly(p-chloroaniline-formaldehyde) | 15 ppm | MSteel | 1 M HCl, 35 °C | 98% | WL | [160] |
Sulfonated chitosan-doped PANI | 40 ppm | MSteel | 0.5 M HCl, RT | 92% | EIS | [161] |
PANI-polyacrylic acid (PAA) composite | 200 ppm | 316 SSteel | 0.5 M HCl, RT | 92% | EIS | [162] |
PANI-palm oil blend | | MSteel | 3% NaCl, RT | 90% | EIS | [163] |
p-Toluene sulfonic acid-doped PANI | | Copper | 0.1 M HCl, RT | 89% | EIS | [164] |
PANI/modified SiO2 composite coating | 50 μm thick coating | Q235 CSteel | 0.1 M H2SO4, RT | 99% | Tafel | [165] |
PANI-graphene nanocomposite film | 6.9 μm thick coating | 310 SSteel | Aerated 5000 ppm NaCl, RT | 97% | EIS | [166] |
PANI/poly(methyl methacrylate) (PMMA) coating | 40-48 μm thick coating | Q235 CSteel | 0.1 M H2SO4, RT | 99% | Tafel | [167] |
Poly(aniline-co-phenetidine)/SiO2 | 65-75 μm thick coating | MSteel | 3.5% NaCl, 25°C | 99% | Tafel | [168] |
Poly(aniline-co-2-pyridylamine-co-2,3-xylidine)/ZnO nanocomposite | 11.05–13.30 μm thick coating | MSteel | 0.1 M HCl, 30 °C | 99% | Tafel | [169] |
Poly(aniline-co-N-methyl aniline) | — | CSteel | 0.1 M HCl | 81% | Tafel | [170] |
|