Research Progress on Durability of Cellulose Fiber-Reinforced Cement-Based Composites
Table 1
Performance of CFs and commonly used fibers.
| Fibers | Density (g/cm3) | Elongation (%) | Tensile strength (MPa) | Young’s modulus (GPa) |
| Cotton fiber | 1.5-1.6 | 7.0-8.0 | 287-597 | 5.5-12.6 | Jute fiber | 1.3 | 1.5-1.8 | 393-773 | 26.5 | Flax fiber | 1.5 | 2.7-3.2 | 345-1035 | 27.6 | Ramie fiber | 1.5 | 3.6-3.8 | 400-938 | 61.4-128.0 | Sisal fiber | 1.5 | 2.0-2.5 | 511-635 | 9.4-22.0 | Coir fiber | 1.2 | 30.0 | 175 | 4.0-6.0 | Cork fiber | 1.5 | — | 1000 | 40.0 | E-glass fiber | 2.5 | 2.5 | 2000–3500 | 70.0 | S-glass fiber | 2.5 | 2.8 | 4570 | 86.0 | Aramid fiber | 1.4 | 3.3-3.7 | 3000-3150 | 63.0-67.0 | Carbon fiber | 1.4 | 1.4-1.8 | 4000 | 230.0-240.0 |
|
|