Study on Compaction and Machinability of Silicon Nitride (Si3N4) Reinforced Copper Alloy Composite through P/M Route
Table 2
Sintering process sequence.
| Sintering process | Temperature | Time | Starting | Ending |
| Heating process | 35°C | 400°C | 50 min | Soaking process | 400°C | 400°C | 40 min | Heating process | 400°C | 500°C | 40 min | Soaking process | 500°C | 500°C | 40 min | Heating process | 500°C | 600°C | 40 min | Soaking process | 600°C | 600°C | 50 min | Allowed to cooling in the furnace | 600°C | 35°C | — |
|
|