Prediction Formula Describing Viscoelasticity of Unvulcanized Rubber Compound Based on Time-Temperature Equivalent Superposition Principle

<div>Curve of horizontal shift-factors <svg height="9.14241pt" id="M19" style="vertical-align:-3.1815pt" version="1.1" viewbox="-0.0498162 -5.96091 13.319 9.14241" width="13.319pt" xmlns="http://www.w3.org/2000/svg" xmlns:xlink="http://www.w3.org/1999/xlink"><g transform="matrix(.013,0,0,-0.013,0,0)"><path d="M545 106L524 126C493 85 467 65 455 65C438 65 427 113 405 238C448 295 498 362 543 439L533 448L478 435C453 386 423 331 398 295H395C370 404 347 448 282 448C169 448 23 309 23 153C23 54 65 -12 128 -12C203 -12 283 70 339 155H341C360 29 380 -12 411 -12C444 -12 491 11 545 106ZM333 204C265 95 210 54 169 54C137 54 113 96 113 171C113 302 191 405 252 405C301 405 318 306 333 204Z"></path></g><g transform="matrix(.0091,0,0,-0.0091,7.059,3.132)"><path d="M592 498C586 556 582 629 581 675H560C545 656 537 650 510 650H115C87 650 74 652 60 675H40C38 620 33 555 28 495H57C69 539 77 568 89 585C102 607 122 616 205 616H267V123C267 44 259 34 168 28V0H454V28C360 34 352 44 352 123V616H422C498 616 514 608 531 584C542 568 552 543 562 495L592 498Z"></path></g></svg> changing with temperature.</div>

International Journal of Polymer Science

fig3

Figure 3

Figure 3: Prediction Formula Describing Viscoelasticity of Unvulcanized Rubber Compound Based on Time-Temperature Equivalent Superposition Principle 