Polymeric Organo-Silane Coatings for Aluminum Alloy Corrosion Protection by Self-Assembled Metho

Yabin Wang, Yanni Li, and Fang Wang

College of Science, Northwest Agriculture & Forest University, XiNong Road No.22, Shannxi-Yangling, 712100, China

Received 14 November 2010; Accepted 5 December 2010

Copyright © 2012 Hindawi Publishing Corporation. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.


The protective performances of coating formed by organo-silane with a linear alkyl chain for promoting aluminum alloy corrosion protection were evaluated by electrochemical techniques. The coatings were self-assembled in the hydrolyzed hydroalcoholic bath of n-octyltriethoxysilane (OS) and cured at hot air oven by different time. The coatings prepared by the less self-assembled number and shorter cured time, were always porous and scarcely protective. On the contrary, those built by the more self-assembled number and the longer cured time had higher coverage on aluminum surface and favorable corrosion resistant property. The best results were obtained when n-octyltri-ethoxysilane (OS) was hydrolyzed 25 h, self-assembling of OS was conducted for five times and the multi-layers were cured at 120 for 1∼2 hours. In this case, the thicker, high cross-linked and more scarcely defective layer was formed on aluminum alloy surface.