Self-Organization-Based Fabrication of Stable Noble-Metal Nanostructures on Large-Area Dielectric Substrates

Figure 10

SERS spectra of MB adsorbed on an 8 nm thick Ag nanostructures on an oxidized Si wafer (red curve; the oxide thickness is 60 nm) and on glass (blue curve). A 2 nm thick adhesion layer of Ti was used in both samples. The deposition was done at α = 70° with rotation. The black curve is the spectrum of MB on Si/SiO2.
158431.fig.0010

We are committed to sharing findings related to COVID-19 as quickly as possible. We will be providing unlimited waivers of publication charges for accepted research articles as well as case reports and case series related to COVID-19. Review articles are excluded from this waiver policy. Sign up here as a reviewer to help fast-track new submissions.