Surface Modification of Zinc with an Oxime for Corrosion Protection in Chloride Medium
Table 3
Electrochemical parameters and inhibition efficiency in 1 M NaCl, for corrosion of surface-treated zinc at different temperatures.
| Conc. of oxime (%) | (mV) | (mV/dec) | (mV/dec) |
(μA/cm2)
| IE (%) |
| At 35°C | | | | | | 0 | 1027 | 117 | 56.6 | 335 | — | 1 | 1028 | 93.7 | 48.3 | 214 | 40 | 3 | 1031 | 85.7 | 34.6 | 161 | 51 | 5 | 1090 | 78.1 | 28.2 | 78 | 76 | 7 | 1110 | 39.3 | 21.6 | 44 | 84 | At 45°C | | | | | | 0 | 1030 | 95.7 | 76.6 | 334 | — | 1 | 1040 | 85.6 | 78.3 | 223 | 35 | 3 | 1070 | 79.7 | 64.6 | 148 | 56 | 5 | 1090 | 62.5 | 68.2 | 68 | 78 | 7 | 1110 | 43.3 | 51.9 | 38 | 86 | At 55°C | | | | | | 0 | 1030 | 104.7 | 76.6 | 334 | — | 1 | 1055 | 94.6 | 78.3 | 210 | 38 | 3 | 1070 | 78.8 | 64.6 | 134 | 60 | 5 | 1100 | 64.5 | 68.2 | 60 | 82 | 7 | 1150 | 44.5 | 51.9 | 35 | 89 |
|
|