Comparison of Corrosion Behavior of Electrochemically Deposited Nano-Cobalt-Coated Ni Sheet

Deptartment of Mechanical Engineering, King Fahd University of Petroleum and Minerals (KFUPM), Dhahran 31261, Saudi Arabia

Received 24 February 2013; Revised 21 August 2013; Accepted 21 August 2013

Academic Editor: Pier P. Piras

Copyright © 2013 Nasser Al-Aqeeli and Ihsan-ul-Haq Toor. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.


Corrosion behavior of nano-coblat-coated Ni sheet was compared with pure Ni and 20% Fe-Ni alloy sheet using potentiodynamic polarization and linear polarization technique in 0.1 M NaCl solution at room temperature. Results showed that corrosion resistance properties of nano-Co-coated Ni sheet were almost same as that of pure Ni sheet, however corrosion resistance of 20% Fe-Ni sheet was decreased significantly. Pitting potential of 20% Fe-Ni sheet was subsequently decreased as compared to pure Ni sheet as well as nano-cobalt-coated Ni sheet. SEM/EDS analysis of the corroded surfaces showed that both pure Ni and nano-coblat-coated Ni sheet did not show any appreciable corrosion however significant corrosion was observed in the case of 20% Fe-Ni sheet.