An Investigation of Chitosan-Grafted-Poly(vinyl alcohol) as an Electrolyte Membrane
Table 3
Mechanical properties of dry and wet membranes at room temperature.
| Membrane | Dry membrane | Wet membrane | Tensile strength | Elongation at break | Young modulus | Tensile strength | Elongation at break | Young modulus | | | | | | |
| Chitosan (CS) | 32.51 | 1.92 | 16.96 | 18.18 | 6.23 | 2.92 | CS_X | 31.45 | 4.23 | 7.43 | 20.65 | 10.27 | 2.01 | CS/PVA | 28.45 | 115.67 | 0.25 | 0.97 | 24.17 | 0.04 | CS/PVA_X | 53.59 | 154.67 | 0.35 | 2.17 | 82.67 | 0.03 | CS-g-PVA/PVA | 9.67 | 107.83 | 0.09 | 9.23 | 125.33 | 0.07 | CS-g-PVA/PVA_X | 17.17 | 134.50 | 0.13 | 15.13 | 162.67 | 0.09 | PVA | 46.86 | 262.50 | 0.18 | 2.05 | 95.22 | 0.02 | PVA_X | 52.99 | 285.43 | 0.19 | 6.63 | 148.22 | 0.04 | Nafion 117 | 28.57 | 260.17 | 0.11 | 20.64 | 121.75 | 0.17 |
|
|