Preparation and Characterization of Magnetic Mesoporous Bioactive Glass/Carbon Composite Scaffolds

Table 2

Structural parameters and drug loading of the Fe-MBG/C and other MBG composite scaffolds.

Samples	𝑆BET; (m^2/g)	𝑉𝑝; (cm^3/g)	𝐷𝑝; (nm)	Porosity; (%)	Compressive strength; (kPa)	Drug loading; (%)	References
0Fe-MBG/C	254.4	0.248	4.4	80.0±2.4	246.5±69.6	16.2^a	/
5Fe-MBG/C	219.3	0.226	3.7	78.1±3.0	284.9±25.5	13.5^a	/
10Fe-MBG/C	189.7	0.189	3.9	79.5±0.8	323.1±77.5	12.6^a	/
MBG	327.3	0.357	4.07	88.6	52.8±12.4	11.3^b	[24]
10Fe-MBG	268	/	4.5	82.9±2.9	46±5.4	12.5^c	[19]
5.0Silk-MBG	/	/	5.0	94.0	250	15.7^d	[26]
60% MBG/PCL	505^e	0.5^e	5.4^e	/	9.3 ± 3.9 MPa^f	/	[28]

aibuprofen loading; ^bgentamicin loading; ^c,ddexamethasone loading; ^ethe surface area, pore volume, and pore size for MBG materials; ^f3D rapid prototyping technique for the fabrication of MBG/PCL scaffolds.