Corrosion and Corrosion Inhibition of High Strength Low Alloy Steel in 2.0 M Sulfuric Acid Solutions by 3-Amino-1,2,3-triazole as a Corrosion Inhibitor

<table>Change of the open-circuit potential versus time for the HSLA steel in 2.0 M H<sub>2</sub>SO<sub>4</sub> solutions in the absence (1) and presence (2) of 1.0 mM ATA and (3) 5.0 mM ATA, respectively.</table>

Journal of Chemistry

fig1

Figure 1

Figure 1: Corrosion and Corrosion Inhibition of High Strength Low Alloy Steel in 2.0 M Sulfuric Acid Solutions by 3-Amino-1,2,3-triazole as a Corrosion Inhibitor 

Figure 1 | Corrosion and Corrosion Inhibition of High Strength Low Alloy Steel in 2.0 M Sulfuric Acid Solutions by 3-Amino-1,2,3-triazole as a Corrosion Inhibitor 