Corrosion and Corrosion Inhibition of High Strength Low Alloy Steel in 2.0 M Sulfuric Acid Solutions by 3-Amino-1,2,3-triazole as a Corrosion Inhibitor

<table>Nyquist plots for the HSLA steel after its immersion for 10 min in 2.0 M H<sub>2</sub>SO<sub>4</sub> solutions in (1) the absence and the presence of (2) 1 mM ATA and (3) 5 mM ATA, respectively.</table>

Journal of Chemistry

fig5

Figure 5

Figure 5: Corrosion and Corrosion Inhibition of High Strength Low Alloy Steel in 2.0 M Sulfuric Acid Solutions by 3-Amino-1,2,3-triazole as a Corrosion Inhibitor 

Figure 5 | Corrosion and Corrosion Inhibition of High Strength Low Alloy Steel in 2.0 M Sulfuric Acid Solutions by 3-Amino-1,2,3-triazole as a Corrosion Inhibitor 