Research Article
Influence of B2O3 and Basicity on Viscosity and Structure of Medium Titanium Bearing Blast Furnace Slag
Table 1
Composition of slag samples.
| Sample number | Composition (wt, %) | Basicity CaO/SiO2 | TiO2 | SiO2 | Al2O3 | CaO | MgO | MnO | V2O5 | FeO | B2O3 |
| 1 | 18.65 | 27.59 | 13.11 | 29.31 | 8.65 | 1.04 | 0.19 | 1.22 | 0 | 1.06 | 2 | 18.46 | 27.31 | 12.98 | 30.01 | 8.56 | 1.03 | 0.19 | 1.21 | 0 | 1.10 | 3 | 18.23 | 26.97 | 12.81 | 30.90 | 8.45 | 1.01 | 0.18 | 1.19 | 0 | 1.15 | 4 | 17.98 | 26.60 | 12.64 | 31.84 | 8.34 | 1.00 | 0.18 | 1.18 | 0 | 1.20 | 5 | 18.46 | 27.31 | 12.98 | 29.01 | 8.56 | 1.03 | 0.19 | 1.21 | 1 | 1.06 | 6 | 18.07 | 26.74 | 12.70 | 29.48 | 8.38 | 1.01 | 0.18 | 1.18 | 2 | 1.10 | 7 | 17.66 | 26.12 | 12.41 | 30.08 | 8.18 | 0.98 | 0.18 | 1.15 | 3 | 1.15 | 8 | 17.25 | 25.52 | 12.12 | 30.61 | 8.00 | 0.96 | 0.17 | 1.13 | 4 | 1.20 |
|
|