Corrosion Performance of Cu-Based Coins in Artificial Sweat
Table 3
Electrochemical parameters of the Cu-based coins evaluated in artificial sweat at 37°C.
| Alloy | (mV) | ba (mV/Dec) | bc (mV/Dec) | (mA/cm2) | (Ohms-cm2) | Zn/Ni ratio |
| Cu | −310 | 300 | 69 | 0.01110 | 2276 | — | 23Ni | −285 | 207 | 67 | 0.00734 | 3085 | — | 32Zn | −347 | 355 | 67 | 0.00854 | 2950 | — | 10Ni25Zn | −332 | 334 | 72 | 0.00941 | 3298 | 2.5 | 13Ni17Zn | −301 | 343 | 62 | 0.00810 | 3236 | 1.3 | 15Ni22Zn | −323 | 230 | 58 | 0.00573 | 2900 | 1.47 | 8Ni27Zn | −271 | 330 | 75 | 0.00406 | 4880 | 3.37 | 6Al2Ni | −344 | 244 | 70 | 0.00624 | 4708 | — | 13Zn6Mn4Ni | −346 | 333 | 68 | 0.00724 | 3350 | 3.25 | 6Zn5Al1Sn | −360 | 195 | 61 | 0.00362 | 4152 | — |
|
|