Investigation into Polyurethane at Varying Dose Rates of Ionizing Radiation for Clinical Application
Table 2
FTIR Peak area data showing slight differences in bonds (
).
| | C-O-C, sym | N-H, C-N | N-H, C-N | C=O stretch | Sym. CH2 | Asym. CH2 | N-H bond |
| Gy·min−1 | 1073 | 1216 | 1524 | 1700 | 2853 | 2933 | 3301 | 3.2 | 0.44 ± 0.01 | 0.64 ± 0.1 | 0.72 ± 0.01 | 0.60 ± 0.01 | 0.49 ± 0.01 | 0.40 ± 0.01 | 0.25 ± 0.0 | 4.5 | 0.54 ± 0.04 | 0.66 ± 0.04 | 0.72 ± 0.03 | 0.57 ± 0.01 | 0.38 ± 0.01 | 0.38 ± 0.02 | 0.23 ± 0.01 | 44 | 0.51 ± 0.04 | 0.65 ± 0.04 | 0.70 ± 0.02 | 0.57 ± 0.02 | 0.46 ± 0.04 | 0.36 ± 0.11 | 0.24 ± 0.01 | 833 | 0.51 ± 0.01 | 0.59 ± 0.01 | 0.71 ± 0.01 | 0.59 ± 0.01 | 0.45 ± 0.02 | 0.39 ± 0.01 | 0.25 ± 0.0 |
|
|