Research Article
Influence of Organoclay on the Flame Retardancy and Thermal Insulation Property of Expandable Graphite/Polyurethane Foam
Table 2
Flame-retardant and physical properties of RPUF composites.
| No. | Sample | HB-rating | V-rating | LOI (vol%) | Stress at 10% strain (Mpa) | Thermal conductivity (W·m−1·K−1) |
| 1 | Pure RPUF | 300 mm/min. –fail | Fail | 20.2 | 0.2464 | 0.028 | 2 | EG5-RPUF | HB | Fail | 23.7 | 0.2421 | 0.036 | 3 | EG10-RPUF | HB | V-0 | 25.9 | 0.2367 | 0.047 | 4 | EG15-RPUF | HB | V-0 | 28.1 | 0.2313 | 0.053 | 5 | EG15-20A2.5-RPUF | HB | V-0 | 28.5 | 0.2485 | 0.048 | 6 | EG15-20A5-RPUF | HB | V-0 | 28.7 | 0.2536 | 0.041 | 7 | EG17.5-RPUF | HB | V-0 | 29.2 | 0.2284 | 0.055 | 8 | EG17.5-20A2.5-RPUF | HB | V-0 | 29.4 | 0.2426 | 0.05 | 9 | EG20-RPUF | HB | V-0 | 30.5 | 0.2217 | 0.058 |
|
|