Research Article
Synthesis and Application of Nanomagnetic Immobilized Phospholipase C
Figure 3
Scanning electron microscopy images of particles prepared and particle size analysis. In (a), the ballability of Fe3O4@SiO2@p(GMA) was good and the average size was 90 nm. In (b), SEM micrographs of PLC-Fe3O4@SiO2@p(GMA) also had a good ballability and the average particle size was about 105 nm. The average particle size of Fe3O4@SiO2@p(GMA) was 96.70 ± 1.00 nm, and the particle size distribution range was 55 to 255 nm. For PLC-Fe3O4@SiO2@p(GMA), the average particle size was 99.86 ± 0.80 nm and 90% of the particles were in the range of 58 to 295 nm. (a) Fe3O4@SiO2@p(GMA). (b) PLC-Fe3O4@SiO2@p(GMA). (c) Particle size analysis.
(a) |
(b) |
(c) |