Synthesis of Propylene Carbonate from Epoxide and CO2 Catalyzed by Carbon Nanotubes Supported Fe1.5PMo12O40

Al-Garni, Tahani; Al-Jallal, Nada; Aouissi, Ahmed

doi:https://doi.org/10.1155/2017/5641604

Journal of Chemistry

On this page

Abstract Introduction Materials and Methods Results and Discussion Conclusions Conflicts of Interest Acknowledgments References Copyright Related Articles

Research Article | Open Access

Volume 2017 | Article ID 5641604 | https://doi.org/10.1155/2017/5641604

Synthesis of Propylene Carbonate from Epoxide and CO₂ Catalyzed by Carbon Nanotubes Supported Fe_1.5PMo₁₂O₄₀

Tahani Al-Garni,¹Nada Al-Jallal,¹and Ahmed Aouissi¹

Academic Editor: Esteban P. Urriolabeitia

Received22 Mar 2017

Revised08 Jun 2017

Accepted22 Jun 2017

Published11 Sept 2017

Abstract

Carbon nanotubes (CNTs) were functionalized and were then used as supports of Fe_1.5PMo₁₂O₄₀ (FePMo) Keggin heteropolyanions catalysts. The characterization of the resulting catalysts was investigated by inductively coupled plasma spectrometry (ICP), Fourier transform infrared (FTIR) spectra, X-ray diffraction (XRD), ultraviolet-visible (UV-Vis) light spectroscopy, and transmission electron microscopy (TEM). FTIR and XRD results confirmed that FePMo was bounded on CNTs successfully and the Keggin structure was preserved. Characterization by TEM showed that solids with high FePMo content exhibited aggregation of FePMo in large particles. The as-prepared catalysts were tested in the synthesis of propylene carbonate (PC) from CO₂ and propylene oxide (PO) in a solvent-free reaction and under mild conditions. Effects of various parameters, such as reaction temperature, reaction time, FePMo content on the support, and catalyst loading on the reaction, were investigated. It has been found that CNTs supported FePMo achieved 57.7% PO conversion and 99.0% PC selectivity, whereas unsupported FePMo led only to 8.5% conversion and 48.6% selectivity. The remarkable enhancement of the catalytic activity over the supported catalyst can be attributed mainly to the better dispersion and reactivity of the FePMo catalyst in the supported material.

1. Introduction

The utilization of carbon dioxide as a raw material for the production of chemicals has attracted much attention [1]. Carbon dioxide has the advantages of being a cheap, nontoxic, and renewable C1 resource, and the development of methods for its activation at mild conditions is an attractive research axis [2, 3]. From the point of view of environment protection and resources availability, the transformation of CO₂ into valuable useful organic compounds represents an interesting alternative carbon feedstock. Unfortunately, carbon dioxide is thermodynamically stable and its activation requires high energy. Nevertheless, numerous reactions involving CO₂ are thermodynamically possible provided that an appropriate catalyst is used. Therefore, the design of a catalyst that can capture, activate, and convert CO₂ into useful chemicals is a key strategy. One of the most promising routes using CO₂ is its insertion into epoxides to form cyclic carbonates. Several homogeneous and heterogeneous catalysts have been explored for this reaction. Homogeneous catalysts include polyoxometalates (POMs) [4], complexes of transition metals (Zn, Al, Cr, Co, Cu, Ni, and Sn) salen porphyrin and phthalocyanine [5–7], ionic liquids [8], and quaternary ammonium salts [9]. Although many homogeneous catalysts were found to be effective at low pressure and temperature [6, 7], the difficult and costly separation of the catalysts from the reaction products represents a serious drawback to their application. Consequently, various heterogeneous catalysts, such as metal oxides [10, 11], immobilized complexes or ionic liquids [12–14], titanosilicates [15], metal-organic frameworks [16–19], and zeolites [19], were tested. However, most of these heterogeneous systems require high pressures and high temperature. Taking into account the fact that several homogeneous based POMs catalysts have proven their performance in the cycloaddition of CO₂ [4, 20], their exploration as heterogeneous catalyst systems is a promising way. It is well known that redox and acid–base properties of POMs can be adjusted by varying the heteroatom, counter anion, and addenda atoms. Moreover, these kinds of materials do not undergo deactivation by water [21–23]. Since polyoxometalates are known to be very active catalysts, it would be advantageous to load them on suitable supports, for example, on carbon nanotubes. Indeed, it has been mentioned in the literature that carbon nanotubes capture large quantities of carbon dioxide. It has been reported that CNTs modified with 3-aminopropyltriethoxysilane have a good potential for CO₂ capture [24, 25]. These features prompted us to investigate the catalytic potential of functionalized CNTs supported POMs for the synthesis of propylene carbonate from propylene oxide and CO₂. The synthesis of PC was achieved under mild conditions without using any solvent, which is attractive from both economic and environmental viewpoints.

2. Materials and Methods

2.1. Materials

Carbon nanotubes (CNTs) (>95%) were purchased from EMFUTUR Technologies. Molybdenum tungstate, Na₂MoO₄·2H₂O (98% purity), and propylene oxide were obtained from WINLAB Ltd., UK.

2.2. Preparation of the Catalysts

2.2.1. Heteropolyoxometalates Catalysts

The H₃PMo₁₂O₄₀ heteropolyacid was prepared according to Rocchiccioli-Deltcheff and Fournier method [26]. The heteropolymolybdate salts, namely, Fe_1.5PMo₁₂O₄₀, Co_1.5PMo₁₂O₄₀, Cu_1.5PMo₁₂O₄₀, and Zn_1.5PMo₁₂O₄₀ (abbreviated as FePMo, CoPMo, CuPMo, and ZnPMo), were prepared as precipitates by slowly adding the required amount of Ba(OH)₂·8H₂O (to neutralize the 3 protons) to the aqueous solution of the H₃PMo₁₂O₄₀ heteropolyacid. Then, the required amount of MSO₄·xH₂O was added (M = Co, Cu, Fe, or Zn), leading to the formation of insoluble barium salt, which was removed by filtration. The resulting solutions were allowed to stand for a few days at 4°C to allow the precipitation of the salts which were then recovered from the solution by filtration.

2.2.2. Immobilization of FePMo on CNTs

To bind FePMo on carbon nanotubes (CNTs) support, oxygenated groups (functionalization) were created by using concentrated nitric acid according to the following steps: 0.1 g of sample of CNTs was suspended in 100 ml of nitric acid (65%) and heated for 5 hours at 80°C and then cooled at room temperature. The treated CNTs were then washed with deionized water at pH 7 and dried at 100°C overnight. The resulting functionalized CNTs were then added to the desired amount of FePMo already dissolved in acetone under stirring and heating at about 60°C until dryness evaporation. The prepared catalyst was dried overnight in an oven at 80°C. Various samples referred to as CNTs-FePMo- ( is the weight in mg of FePMo per 100 mg of CNTs) were prepared.

2.3. Characterization of the Catalysts

Infrared spectra were recorded with an infrared spectrometer GENESIS II-FTIR (4000–400 cm⁻¹) using the KBr Pellet technique. X-ray diffraction (XRD) measurements were carried out employing an Ultima IV X-ray Rigaku diffractometer using Cu-Kα radiation. Elemental analyses were carried out under inductively coupled plasma (ICP) spectrometry measurements using a PerkinElmer Nexion 300D Spectrometer. The UV-Vis spectra (in H₂O) were obtained with a double beam UV-Vis spectrophotometer (Philips 8800). Field emission transmission electron microscopy (TEM) experiments were performed on a JEOL JEM-2100F field emission electron microscope (JEOL, Japan) with an acceleration voltage of 110 kV.

2.4. General Procedure for Synthesis of PC

The reaction of propylene oxide and CO₂ was carried out in 80 mL stainless steel autoclave equipped with a magnetic stirrer. The temperature of the autoclave was adjusted by a heating jacket. In a typical experiment, catalyst, cocatalyst, and propylene oxide were charged into the reactor vessel without using any cosolvent. The reactor vessel was placed under a constant pressure of carbon dioxide and then heated to the required temperature and continuously stirred. When the desired reaction temperature was attained, the reaction mixture was pressurized with CO₂, while stirring, up to the desired level. When the desired time elapsed, the reactor was cooled by ice bath to room temperature and depressurized to atmospheric pressure. The products were analyzed with a gas phase chromatograph (PYE UNICAM) equipped with a flame ionization detector using a capillary column (HP-PLOT Q length 30 mID 0.53 mm). The identification of the products was achieved occasionally by gas chromatography-mass spectrometry (GC-MS) using a Thermo Trace GC Ultra gas chromatograph equipped with AI 3000. For the separation of target compounds, a TR-5 MS-SQC capillary column (30 m × 0.25 mm i.d., phase thickness 0.25 μm) was used with helium as the carrier gas (at a flow rate of 1 mL/min).

3. Results and Discussion

3.1. Catalysts Characterization

3.1.1. Unsupported Heteropolyanions

Elemental analysis of the series of unsupported heteropolyanions salt catalysts was performed by ICP-MS and the results are reported in Table 1. The results were adjusted considering 1 atom of phosphorus per Keggin unit according to the nature of Keggin structure and were found to be in good agreement with the expected ones for molybdenum and counter ion.

The observed frequencies and assignments of the IR bands are given in Table 2. The four bands observed and assigned to the asymmetric stretching vibrations of the (P-Oa), (Mo-Od), (Mo-Oc-Mo), and (Mo-Oc-Mo) bonds are the main characteristic bands of the Keggin structure [26, 27]. In Keggin structure, Oa is the oxygen atom common to PO₄ tetrahedron and one trimetallic group Mo₃O₁₃, Ob is the oxygen shared by two trimetallic groups, Oc binds two octahedral trimetallic groups MoO₆, and Od refers to the terminal oxygen atom.

3.1.2. CNTs Supported Heteropolyanions

Figure 1 shows the IR spectra of the CNTs support and the CNTs-FePMo- catalysts. As already reported in a previous paper [28], oxidized CNTs exhibit, in the 1300–1900 cm⁻¹ range, three main bands at 1386, 1720, and 1585 cm⁻¹ assigned to C-O, C=O, and C=C groups, respectively. In the 3000–4000 cm⁻¹ range, two bands, one at 3448 cm⁻¹ and the other at 3720 cm⁻¹, are assigned to O-H and –COOH groups, respectively. As for the IR spectra of the CNTs supported catalysts, it can be seen that, for all the catalysts, the main characteristic bands of the Keggin structure were observed in the fingerprint region (700–1100 cm⁻¹), indicating that the Keggin structure was maintained. The characteristic bands of FePMo, observed at 1065.42 cm⁻¹, 963.22 cm⁻¹, 869.94 cm⁻¹, and 781.21 cm⁻¹, indicated that the Keggin structure was preserved on the support [26, 27].

3.1.3. X-Ray Diffraction

The XRD patterns of the CNTs, FePMo, and CNTs-FePMo- are illustrated in Figure 2. The three peaks at 26.1°, 43.1°, and 53.5° observed in the XRD pattern of the oxidized CNTs which were indexed to the (002), (100), and (004) diffractions of hexagonal graphite [29, 30], respectively, indicated that the graphitic structure of the CNTs was not destroyed after oxidation treatment. The reflections at 7.2°, 20.5°, and 27.2°, observed in the pattern of FePMo, are the characteristic peaks of the Keggin structure of the phosphomolybdate phase [31]. These diffraction peaks could be readily indexed to cubic structure (JCPDS 09-0412). In the case of CNTs-FePMo- catalysts, the characteristic lines of the Keggin structure at 25.6° and 29.7° can be observed easily for the samples with high FePMo content, showing that the Keggin structure was preserved on the support. It is worth noting that the intensity of the hexagonal graphite structure on CNTs was stronger than that of CNTs-FePMo- samples. A similar finding was observed by Li et al. [32]. In fact, when comparing the XRD patterns of pure CNTs and Fe₃O₄-CNTs nanocomposite, they found that the intensity of the pure CNTs was stronger than that of Fe₃O₄-CNTs nanocomposite. In the opinion of the authors, this might be due to the fact that grafted Fe₃O₄ on the CNTs surface weakened the diffraction peak at 26.1°. Thus, the XRD patterns combined with FTIR spectra indicated that the active phase FePMo on CNT conserved the Keggin-type structure and the as-prepared CNTs-FePMo- catalysts were successfully synthesized.

3.1.4. UV-Visible Spectroscopy

The amount of FeMo₁₂ loaded on CNTs support was determined by using the UV-visible technique. The UV-visible spectrum of the Keggin FePMo sample shows a large band with multiplicity in the domain of wavelengths 250–500 nm. According to the literature, this band constituted several components, due to the changes from the double-occupied oxo orbital to the unoccupied Mo d orbitals () in the Keggin anion [33, 34]. It constituted several components (200–250, 270–350, and 400–450 nm ranges) having different energies associated with ligand–metal charge transfers from oxygen to . The results of FeMo₁₂ loaded on CNTS support in aqueous solution, reported in Table 3, showed that the nominal concentrations were slightly different from the experimental ones.

3.1.5. Transmission Electronic Microscopy

The results of TEM analysis of the functionalized CNTs support and the CNTs-FePMo- supported catalysts are shown in Figure 3. It can be seen that at lower contents FePMo clusters are well dispersed ((b), (c), and (d)) while at higher contents ((e) and (f)) agglomeration into larger crystallites is formed. The aggregation of FePMo clusters into large particles at high contents might be due to the insufficient number of binding sites (functional groups) to anchor all the FePMo particles.

(a)

(b)

(c)

(d)

(e)

(f)

3.2. Catalytic Activity

3.2.1. Effect of Counter Ion

The experiments were carried out at 65°C during a period of 7 h under 5-bar CO₂ pressure using 0.150 g of the catalyst and 0.050 g of tetraethyl ammonium bromide (TEABr) as a cocatalyst. The results are shown in Table 4. It can be seen that ZnPMo led to the highest selectivity in PC (56.2%) but to the lowest conversion (2.86%), whereas FePMo catalyst led to the highest conversion (8.45%) and to a relatively higher selectivity in PC (48.6%). These results indicated that FePMo was the suitable catalyst for the conversion of PO into PC. Therefore, it was selected for further investigations such as the effect of reaction temperature, content on CNTs support, and reaction time.

3.2.2. Effect of Temperature

The selected FePMo catalyst was tested for the reaction of PO with CO₂ at different reaction temperatures. The experiments were carried out under a pressure of CO₂ equal to 5 bar for 7 hours. The results depicted in Figure 4 showed that the temperature has a strong effect on the conversion. With the increase of temperature from 55 to 65°C, PO conversion increased sharply from 5.46 to 8.92%. Further rise of temperature to 85°C resulted in only a slight increase of PO conversion (9.94%) due to the decrease of CO₂ solubility in the reaction mixture. In fact, an increase in the reaction temperature increased the conversion but at the same time decreased the solubility of carbon dioxide in the reaction system. A similar finding was reported in the literature [35, 36]. Contrary to PO conversion, PC selectivity decreased slightly and can be considered as remaining unchanged as the temperature increased. This very slight decrease in the selectivity of PC might be caused by the increase of secondary reactions such as isomerization to acetone, as well as the hydrolysis to diol, favored at high temperatures [37, 38]. Based on the above results, it can be concluded that 65°C was the optimum reaction temperature and all the subsequent experiments for PC synthesis were performed at this temperature.

3.2.3. Effect of CNTs Support

It is well known that both the conversion and the selectivity depend on the size and dispersion of the catalyst particles on the support. A strong interaction between the particles and the support leads to high dispersion of the particles on the support which in turn leads to high conversion and selectivity. Functionalized CNTs are among the supports that possess these properties. Moreover, they have high specific surface areas, good thermal properties, and excellent adsorption properties [39]. That is why we have selected CNTs as a catalyst support to investigate the influence of FePMo content on PO conversion. The experiments were carried out at 65°C under 5-bar CO₂ pressure during a period of 7 hours and the results are shown in Figure 5. As expected, PO conversion increased with increasing FePMo content, whereas PC selectivity decreased slightly. This result can be explained by the fact that, at high loading, the amount of FePMo loaded on the CNTs was larger than the available functional groups created on the support, which influenced the dispersion of FePMo on the support. When the concentration of the functional groups is less than that of the FePMo particles on the support, there will be poor dispersion (aggregation) of FePMo particles (as evidenced by TEM) and consequently the selectivity decreases. Similar findings were observed by the authors of [40] in their study of the hydrogenation of phenylacetylene over CNTs supported Pt catalyst. The authors mentioned that the high conversion and selectivity to styrene obtained might be due to the higher dispersion (i.e., smaller particle size) of the Pt particles size.

3.2.4. Effect of Reaction Time

The influence of reaction time on PO conversion and PC selectivity was investigated in the time interval 3–7 h. The experiments were performed using CNT-FePMo-350 catalyst at 65°C under CO₂ pressure of 5 bar and the results are depicted in Figure 6. It is observed that the conversion of PO increases progressively, reaching PO conversion of 47.1% at 7 hours, whereas the selectivity of the PC increases within the first 5 hours only. Beyond 5 hours, it remains approximatively at 75% throughout.

3.2.5. Effect of Catalyst Amount

The effect of the amount of CNTs-FePMo-350 on the conversion and selectivity was investigated in the range of 0.15–0.3 g at 65°C for 7 h under a 5-bar CO₂ pressure. The results depicted in Figure 7 showed that when the catalyst amount was increased from 0.15 g to 3 g, the conversion increased from 26.6% to 57.7%, whereas no significant change in the selectivity was observed. Compared to the unsupported FePMo catalyst, CNTs supported FePMo enhanced the conversion of epoxide remarkably. Conversion of 57.7% and selectivity of 99% were achieved, whereas unsupported FePMo led only to 8.5% conversion and 48.6% selectivity. The enhancement in activity of CNT-FePMo catalyst can be attributed to the capture of CO₂ by the highest porous CNTs combined with the highest activity of FePMo and also by the high dispersion of FePMo clusters owing to the oxygenated groups created on the CNTs [41, 42]. Thus, CNTs play a role not only in increasing the dispersion of FePMo clusters, but also in lowering the high pressure required to dissolve CO₂ gas in the reactant mixture. It is worth noting that most of the reactions of cyclic carbonate involving CO₂ gas, reported in the literature, were carried out under very high pressure of CO₂ [36, 37, 43, 44]. In our research work, experiments were carried out under mild conditions, that is, 65°C and 5 bar.

3.2.6. Effect of CO₂ Pressure

Figure 8 depicts the effect of CO₂ pressure on the conversion and selectivity of PC. It can be seen that the conversion depends strongly on the CO₂ pressure. Indeed, when CO₂ pressure was increased from 5 to 8 bar, the conversion increased from 47.1% to 64.6%, which represents an increase of 27%. Further increase in CO₂ pressure led to a slight decrease in the conversion. This can be explained by the pressure effect on the concentrations of CO₂ and epoxide in the two phases of reaction medium [45]. The top phase is the CO₂-rich phase, and the bottom phase is the epoxide-rich phase. The reactions occur in the liquid phase because of the presence of the catalyst in this phase. The conversion increased when the concentration of CO₂ increased in the bottom phase at low pressure, and decreased when the concentration of PO decreased in the bottom phase at high pressure (>9 bar). As for PC selectivity, it can be seen that CO₂ pressure has no significant influence. It can be concluded from this result that 8-bar CO₂ pressure is the optimized condition for the synthesis of PC from PO and CO₂ for the reaction conducted at 65°C over CNTs-FePMo catalyst system.

4. Conclusions

A series of unsupported Keggin-type heteropolyanions (M_1.5PMo₄₀, M = Zn, Cu, Co, and Fe) and a series of CNTs supported FePMo heteropolyanions were prepared and characterized by means of ICP, FTIR, XRD, UV, and TEM. It has been found that the Keggin structure of FePMo heteropolyanions was preserved on the CNTs support.

The as-prepared catalysts were tested for the reaction of carbon dioxide with propylene oxide. It has been found that the heteropolyanions having Fe as counter anion (FePMo) were the most active of the series of unsupported catalysts. When supported on CNTs, FePMo exhibited high catalytic performance compared to the unsupported FePMo.

The enhanced activity can be attributed mainly to the better dispersion and reactivity of the FePMo catalyst in the supported material.

The CNTs play a role not only as a solid support to heterogenize the catalyst for easy separation, but also in lowering the high pressure required to dissolve CO₂ gas in the reactant mixture.

The reaction of propylene oxide with CO₂ leading to propylene carbonate can be catalyzed by CNT-FePMo, with high conversion and selectivity without using a solvent and under mild reaction conditions (temperature of 65°C and CO₂ pressure of 5 bar).

Conflicts of Interest

The authors declare that there are no conflicts of interest regarding the publication of this paper.

Acknowledgments

The authors would like to extend their appreciation to the Deanship of Scientific Research at King Saud University for funding the work through the Research Group Project no. RGP-VPP-116.

References

R. W. Dorner, D. R. Hardy, F. W. Williams, and H. D. Willauer, “Heterogeneous catalytic CO2 conversion to value-added hydrocarbons,” Energy and Environmental Science, vol. 3, no. 7, pp. 884–890, 2010.
View at: Publisher Site | Google Scholar
M. Mikkelsen, M. Jørgensen, and F. C. Krebs, “The teraton challenge. A review of fixation and transformation of carbon dioxide,” Energy and Environmental Science, vol. 3, no. 1, pp. 43–81, 2010.
View at: Publisher Site | Google Scholar
T. Sakakura, J.-C. Choi, and H. Yasuda, “Transformation of carbon dioxide,” Chemical Reviews, vol. 107, no. 6, pp. 2365–2387, 2007.
View at: Publisher Site | Google Scholar
H. Yasuda, L.-N. He, T. Sakakura, and C. Hu, “Efficient synthesis of cyclic carbonate from carbon dioxide catalyzed by polyoxometalate: The remarkable effects of metal substitution,” Journal of Catalysis, vol. 233, no. 1, pp. 119–122, 2005.
View at: Publisher Site | Google Scholar
D. Bai, X. Wang, Y. Song et al., “Bifunctional metalloporphyrins-catalyzed coupling reaction of epoxides and CO2 to cyclic carbonates,” Cuihua Xuebao/Chinese Journal of Catalysis, vol. 31, no. 2, pp. 176–180, 2010.
View at: Publisher Site | Google Scholar
C. J. Whiteoak, E. Martin, M. M. Belmonte, J. Benet-Buchholz, and A. W. Kleij, “An efficient iron catalyst for the synthesis of five- and six-membered organic carbonates under mild conditions,” Advanced Synthesis and Catalysis, vol. 354, no. 2-3, pp. 469–476, 2012.
View at: Publisher Site | Google Scholar
Y. Yang, Y. Hayashi, Y. Fujii et al., “Efficient cyclic carbonate synthesis catalyzed by zinc cluster systems under mild conditions,” Catalysis Science and Technology, vol. 2, no. 3, pp. 509–513, 2012.
View at: Publisher Site | Google Scholar
J. Sun, J. Ren, S. Zhang, and W. Cheng, “Water as an efficient medium for the synthesis of cyclic carbonate,” Tetrahedron Letters, vol. 50, no. 4, pp. 423–426, 2009.
View at: Publisher Site | Google Scholar
H.-Y. Ju, M.-D. Manju, K.-H. Kim, S.-W. Park, and D.-W. Park, “Catalytic performance of quaternary ammonium salts in the reaction of butyl glycidyl ether and carbon dioxide,” Journal of Industrial and Engineering Chemistry, vol. 14, no. 2, pp. 157–160, 2008.
View at: Publisher Site | Google Scholar
K. Yamaguchi, K. Ebitani, T. Yoshida, H. Yoshida, and K. Kaneda, “Mg-Al mixed oxides as highly active acid-base catalysts for cycloaddition of carbon dioxide to epoxides,” Journal of the American Chemical Society, vol. 121, no. 18, pp. 4526-4527, 1999.
View at: Publisher Site | Google Scholar
M. Aresta, A. Dibenedetto, L. Gianfrate, and C. Pastore, “Enantioselective synthesis of organic carbonates promoted by Nb(IV) and Nb(V) catalysts,” Applied Catalysis A: General, vol. 255, no. 1, pp. 5–11, 2003.
View at: Publisher Site | Google Scholar
L. Han, H. Li, S.-J. Choi et al., “Ionic liquids grafted on carbon nanotubes as highly efficient heterogeneous catalysts for the synthesis of cyclic carbonates,” Applied Catalysis A: General, vol. 429-430, pp. 67–72, 2012.
View at: Publisher Site | Google Scholar
D. Bai, Q. Wang, Y. Song, B. Li, and H. Jing, “Synthesis of cyclic carbonate from epoxide and CO₂ catalyzed by magnetic nanoparticle-supported porphyrin,” Catalysis Communications, vol. 12, no. 7, pp. 684–688, 2011.
View at: Publisher Site | Google Scholar
J. Meléndez, M. North, P. Villuendas, and C. Young, “One-component bimetallic aluminium(salen)-based catalysts for cyclic carbonate synthesis and their immobilization,” Dalton Transactions, vol. 40, no. 15, pp. 3885–3902, 2011.
View at: Publisher Site | Google Scholar
D. Srinivas and P. Ratnasamy, “Spectroscopic and catalytic properties of SBA-15 molecular sieves functionalized with acidic and basic moieties,” Microporous and Mesoporous Materials, vol. 105, no. 1-2, pp. 170–180, 2007.
View at: Publisher Site | Google Scholar
J. Song, Z. Zhang, S. Hu, T. Wu, T. Jiang, and B. Han, “MOF-5/n-Bu4NBr: An efficient catalyst system for the synthesis of cyclic carbonates from epoxides and CO2 under mild conditions,” Green Chemistry, vol. 11, no. 7, pp. 1031–1036, 2009.
View at: Publisher Site | Google Scholar
H.-Y. Cho, D.-A. Yang, J. Kim, S.-Y. Jeong, and W.-S. Ahn, “CO₂ adsorption and catalytic application of Co-MOF-74 synthesized by microwave heating,” Catalysis Today, vol. 185, no. 1, pp. 35–40, 2012.
View at: Publisher Site | Google Scholar
X. Zhou, Y. Zhang, X. Yang, L. Zhao, and G. Wang, “Functionalized IRMOF-3 as efficient heterogeneous catalyst for the synthesis of cyclic carbonates,” Journal of Molecular Catalysis A: Chemical, vol. 361-362, pp. 12–16, 2012.
View at: Publisher Site | Google Scholar
R. Srivastava, D. Srinivas, and P. Ratnasamy, “Zeolite-based organic-inorganic hybrid catalysts for phosgene-free and solvent-free synthesis of cyclic carbonates and carbamates at mild conditions utilizing CO2,” Applied Catalysis A: General, vol. 289, no. 2, pp. 128–134, 2005.
View at: Publisher Site | Google Scholar
F. Chen, T. Dong, Y. Chi, Y. Xu, and C. Hu, “Transition-metal-substituted keggin-type germanotungstates for catalytic conversion of carbon dioxide to cyclic carbonate,” Catalysis Letters, vol. 139, no. 1-2, pp. 38–41, 2010.
View at: Publisher Site | Google Scholar
Y.-F. Song and R. Tsunashima, “Recent advances on polyoxometalate-based molecular and composite materials,” Chemical Society Reviews, vol. 41, no. 22, pp. 7384–7402, 2012.
View at: Publisher Site | Google Scholar
K. W. La, J. C. Jung, H. Kim, S.-H. Baeck, and I. K. Song, “Effect of acid-base properties of H3PW12O40/CexTi1-xO2 catalysts on the direct synthesis of dimethyl carbonate from methanol and carbon dioxide: A TPD study of H3PW12O40/CexTi1-xO2 catalysts,” Journal of Molecular Catalysis A: Chemical, vol. 269, no. 1-2, pp. 41–45, 2007.
View at: Publisher Site | Google Scholar
C. Jiang, Y. Guo, C. Wang, C. Hu, Y. Wu, and E. Wang, “Synthesis of dimethyl carbonate from methanol and carbon dioxide in the presence of polyoxometalates under mild conditions,” Applied Catalysis A: General, vol. 256, no. 1-2, pp. 203–212, 2003.
View at: Publisher Site | Google Scholar
F. Su, C. Lu, W. Cnen, H. Bai, and J. F. Hwang, “Capture of CO2 from flue gas via multiwalled carbon nanotubes,” Science of the Total Environment, vol. 407, no. 8, pp. 3017–3023, 2009.
View at: Publisher Site | Google Scholar
C. Lu, H. Bai, B. Wu, F. Su, and J. F. Hwang, “Comparative study of CO2 capture by carbon nanotubes, activated carbons, and zeolites,” Energy and Fuels, vol. 22, no. 5, pp. 3050–3056, 2008.
View at: Publisher Site | Google Scholar
C. Rocchiccioli-Deltcheff and M. Fournier, “Catalysis by polyoxometalates. Part 3.—influence of vanadium(V) on the thermal stability of 12-metallophosphoric acids from in situ infrared studies,” Journal of the Chemical Society, Faraday Transactions, vol. 87, no. 24, pp. 3913–3920, 1991.
View at: Publisher Site | Google Scholar
C. Rocchiccioli-Deltcheff, M. Fournier, R. Franck, and R. Thouvenot, “Vibrational investigations of polyoxometalates. 2. Evidence for anion-anion interactions in molybdenum(VI) and tungsten(VI) compounds related to the keggin structure,” Inorganic Chemistry, vol. 22, no. 2, pp. 207–216, 1983.
View at: Publisher Site | Google Scholar
A. Al-Mayouf, M. Saleh, A. Aouissi, and A. Al-Suhybani, “Catalytic Performance of Carbon Nanotubes Supported 12-Tungstosilicic Acid in the Electrooxidation of Cyclohexane to Cyclohexanone and Cyclohexanol,” Journal of Chemical Engineering & Process Technology, vol. 05, no. 01, p. 183, 2014.
View at: Publisher Site | Google Scholar
H. Zhang, G. Lin, Z. Zhou, X. Dong, and T. Chen, “Raman spectra of MWCNTs and MWCNT-based H₂ adsorbing system,” Carbon, vol. 40, no. 13, pp. 2429–2436, 2002.
View at: Publisher Site | Google Scholar
Z. Sun, Z. Liu, B. Han et al., “Fabrication of ruthenium-carbon nanotube nanocomposites in supercritical water,” Advanced Materials, vol. 17, no. 7, pp. 928–932, 2005.
View at: Publisher Site | Google Scholar
M. Fournier, C. Feumi-Jantou, C. Rabia, G. Hervé, and S. Launay, “Polyoxometalates catalyst materials: X-ray thermal stability study of phosphorus-containing heteropolyacids H3+xPM12-xVxO40·13-14H 2O (M=Mo,W; x=0-1),” Journal of Materials Chemistry, vol. 2, no. 9, pp. 971–978, 1992.
View at: Publisher Site | Google Scholar
S. Li, Y. Gong, Y. Yang et al., “Recyclable CNTs/Fe3O4 magnetic nanocomposites as adsorbents to remove bisphenol A from water and their regeneration,” Chemical Engineering Journal, vol. 260, pp. 231–239, 2015.
View at: Publisher Site | Google Scholar
L. Dermeche, R. Thouvenot, S. Hocine, and C. Rabia, “Preparation and characterization of mixed ammonium salts of Keggin phosphomolybdate,” Inorganica Chimica Acta, vol. 362, no. 11, pp. 3896–3900, 2009.
View at: Publisher Site | Google Scholar
F. Cavani, R. Mezzogori, A. Pigamo, and F. Tifirò, “Modification of redox and catalytic properties of Keggin-type, Sb-doped P/Mo polyoxometalates in the selective oxidation of isobutane to methacrylic acid: Control of preparation conditions,” Studies in Surface Science and Catalysis, vol. 140, pp. 141–152, 2001.
View at: Publisher Site | Google Scholar
C. Jing-Xian, J. Bi, D. Wei-Li et al., “Catalytic fixation of CO2 to cyclic carbonates over biopolymer chitosan-grafted quarternary phosphonium ionic liquid as a recylable catalyst,” Applied Catalysis A: General, vol. 484, pp. 26–32, 2014.
View at: Publisher Site | Google Scholar
L. Han, H.-J. Choi, S.-J. Choi, B. Liu, and D.-W. Park, “Ionic liquids containing carboxyl acid moieties grafted onto silica: Synthesis and application as heterogeneous catalysts for cycloaddition reactions of epoxide and carbon dioxide,” Green Chemistry, vol. 13, no. 4, pp. 1023–1028, 2011.
View at: Publisher Site | Google Scholar
J. Sun, J. Wang, W. Cheng et al., “Chitosan functionalized ionic liquid as a recyclable biopolymer-supported catalyst for cycloaddition of CO₂,” Green Chemistry, vol. 14, no. 3, pp. 654–660, 2012.
View at: Publisher Site | Google Scholar
T.-Y. Shi, J.-Q. Wang, J. Sun, M.-H. Wang, W.-G. Cheng, and S.-J. Zhang, “Efficient fixation of CO₂ into cyclic carbonates catalyzed by hydroxyl-functionalized poly (ionic liquids),” RSC Advances, vol. 3, no. 11, pp. 3726–3732, 2013.
View at: Publisher Site | Google Scholar
P. Serp, M. Corrias, and P. Kalck, “Carbon nanotubes and nanofibers in catalysis,” Applied Catalysis A: General, vol. 253, no. 2, pp. 337–358, 2003.
View at: Publisher Site | Google Scholar
C. Li, Z. Shao, M. Pang, C. T. Williams, and C. Liang, “Carbon nanotubes supported Pt catalysts for phenylacetylene hydrogenation: Effects of oxygen containing surface groups on Pt dispersion and catalytic performance,” Catalysis Today, vol. 186, no. 1, pp. 69–75, 2012.
View at: Publisher Site | Google Scholar
L. Liu and S. K. Bhatia, “Molecular simulation of CO2 adsorption in the presence of water in single-walled carbon nanotubes,” Journal of Physical Chemistry C, vol. 117, no. 26, pp. 13479–13491, 2013.
View at: Publisher Site | Google Scholar
M. E. Casco, A. Morelos-Gómez, S. M. Vega-Díaz et al., “CO2 adsorption on crystalline graphitic nanostructures,” Journal of CO2 Utilization, vol. 5, pp. 60–65, 2014.
View at: Publisher Site | Google Scholar
W.-L. Dai, B. Jin, S.-L. Luo, X.-B. Luo, X.-M. Tu, and C.-T. Au, “Functionalized phosphonium-based ionic liquids as efficient catalysts for the synthesis of cyclic carbonate from expoxides and carbon dioxide,” Applied Catalysis A: General, vol. 470, pp. 183–188, 2014.
View at: Publisher Site | Google Scholar
G. Zhao, Y. Zhang, H. Zhang, J. Li, and S. Gao, “Direct synthesis of propylene carbonate from propylene and carbon dioxide catalyzed by quaternary ammonium heteropolyphosphatotungstate-TBAB system,” Journal of Energy Chemistry, vol. 24, no. 3, pp. 353–358, 2015.
View at: Publisher Site | Google Scholar
Y. Xiong, F. Bai, Z. Cui, N. Guo, and R. Wang, “Cycloaddition reaction of carbon dioxide to epoxides catalyzed by polymer-supported quaternary phosphonium salts,” Journal of Chemistry, vol. 2013, Article ID 261378, 9 pages, 2013.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2017 Tahani Al-Garni et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

3250

Downloads

1340

Citations