Thermomechanical Impact of Polyurethane Potting on Gun Launched Electronics
Table 3
Input for viscoelastic prony parameter calibration, hot.
|
*real |
*imaginary |
*real |
*imaginary | Frequency (Hz) |
| 0.2061 | 0.00000 | 0.00000 | 0.00000 | 1.0 | 0.1274 | −0.02513 | 0.00000 | 0.00000 | 1.5 | 0.1464 | −0.04945 | 0.00000 | 0.00000 | 2.5 | 0.1723 | −0.07912 | 0.00000 | 0.00000 | 3.9 | 0.2074 | −0.1149 | 0.00000 | 0.00000 | 6.3 | 0.252 | −0.1598 | 0.00000 | 0.00000 | 10.0 | 0.3111 | −0.2163 | 0.00000 | 0.00000 | 15.8 | 0.3957 | −0.2878 | 0.00000 | 0.00000 | 25.1 | 0.4926 | −0.3817 | 0.00000 | 0.00000 | 39.8 | 0.6204 | −0.4866 | 0.00000 | 0.00000 | 63.0 | 0.8108 | −0.5726 | 0.00000 | 0.00000 | 100.0 |
|
|