Effect of SiC Addition on Microhardness and Relative Density during Selective Laser Melting of 316L Stainless Steel

Table 2

The sample produced with constant layer thickness of 30 µm, hatch distance of 70 µm, and laser power of 200 W.

No. of sample	Scanning speed (mm/s)	VED (J/mm^3)	Microhardness (HV)
S1	500	190	277
S2	600	158	284
S3	700	136	296
S4	800	119	292