Resin Composite Materials for Chairside CAD/CAM Restorations: A Comparison of Selected Mechanical Properties
Table 2
Mechanical properties of the testing materials.
| Material | σf (MPa) | Ef (GPa) | HV01 | m | σ0 (MPa) | x̅ (SD) | x̅ (SD) | x̅ (SD) |
| GR | 186.02 (10.49) A | 16.95 (0.50) A | 140.43 (5.47) A | 25.72 | 190.30 | TE | 170.65 (5.61) B | 10.56 (0.19) B | 74.88 (2.82) BC | 34.89 | 173.26 | CR | 170.46 (8.89) B | 11.14 (0.16) C | 75.40 (2.18) B | 27.18 | 174.16 | AV | 142.79 (6.56) C | 8.39 (0.13) D | 70.85 (1.62) C | 22.92 | 145.90 | CS | 136.27 (9.40) C | 8.45 (0.20) D | 71.13 (0.92) BC | 16.35 | 140.50 | HC | 120.38 (6.54) D | 8.26 (0.55) D | 77.84 (5.11) B | 19.62 | 123.45 | value | | | | — | — |
|
|