Low-Temperature Preparation of Amorphous-Shell/ Nanocrystalline-Core Nanostructured Electrodes for Flexible Dye-Sensitized Solar Cells
Figure 3
Photocurrent-voltage
characteristic of a cell based on the amorphous shell/nanocrystalline core nanostructured
TiO2 electrode after sintering. Light intensity was 100 mW/cm2. Electrode area was 0.28 cm2.