Effect of Carbon Nanofiber-Matrix Adhesion on Polymeric Nanocomposite Properties—Part II
Table 5
Thermal and
electrical properties of nanocomposites as a function of treatment time.
| | Sample | Surface treatment | Mass | Resistivity | K | Density | | time (min) | % | (Ohm-cm) | (W/m-K) | (g/cm3)
|
| | EPON 862 | — | 0 | 3.28E
+ 10 | 0.1768 | 1.198 | | PR-24-PS | 0 | 12 | 1.58E
+ 00 | 0.3731 | 1.252 | | PR-24-PS-ET
(0.5) | 0.5 | 12 | 4.13E
+ 00 | 0.2992 | 1.237 | | PR-24-PS-ET
(1) | 1 | 12 | 5.16E
+ 01 | 0.3476 | 1.253 | | PR-24-PS-ET
(2) | 2 | 12 | 3.14E
+ 03 | 0.3303 | 1.246 | | PR-24-PS-ET
(4) | 4 | 12 | 5.57E
+ 06 | 0.3032 | 1.240 | | PR-24-PS-ET
(8) | 8 | 12 | 3.35E
+ 07 | 0.3290 | 1.235 | | PR-24-PS-ET
(10) | 10 | 12 | 5.56E
+ 10 | 0.3334 | 1.257 | | PR-24-PS-ET
(12) | 12 | 12 | 4.54E
+ 09 | 0.3493 | 1.234 | | PR-24-PS-ET
(15) | 15 | 12 | 3.69E
+ 10 | 0.3348 | 1.254 |
|
|