Enhancement of Ammonia Sensitivity in Swift Heavy Ion Irradiated Nanocrystalline
Thin Films
Table 1
Sensitivity factors of unirradiated and irradiated SnO
2
thin films for ammonia and ethanol at different temperatures.
Ni
+
ion irradiation fluence
Temperature
(sensitivity %)
Temperature
(sensitivity %)
Temperature
(sensitivity %)
Unirradiated
52
5
98
32
284
87
ions/cm
2
68
15
103
53
516
115
ions/cm
2
122
27
649
73
882
142