Performance Enhancement of Dental Composites Using Electrospun Nanofibers
Table 2
Mechanical properties of QC STD H UF as a function of electrospun nanofibers.
| mechanical property | concentration [%wt.] | PVOH nanofibers | PLLA nanofibers | PA6 nanofibers | 250 nm | 125 nm | 250 nm | 250 nm | 125 nm | 250 nm |
| CS [Mpa] | 0 | 184.0 | 184.0 | 184.0 | 184.0 | 184.0 | 184.0 | 0.01 | 121.4 | 140.7 | 137.2 | 136.2 | 144.2 | 132.1 | 0.05 | 213.9 | 126.4 | 206.3 | 165 | 182.1 | 77.8 | 0.1 | 138.2 | 100.5 | 145.3 | 143.9 | 133.3 | 63.1 | 0.3 | 89.9 | 94.1 | 115.6 | 94.0 | 125.0 | 67.6 | P [ANOVA] | 0.003 | 0.002 | 0.0003 | 0.004 | 0.05 | 4.35E-9 | () | () | () | () | () | () |
|
DTS [Mpa] | 0 | 30 | 30 | 30 | 30 | 30 | 30 | 0.01 | 22.3 | 27.5 | 28.9 | 30.0 | 28.6 | 31.9 | 0.05 | 27.8 | 27.6 | 29.5 | 24.9 | 27.6 | 20.8 | 0.1 | 21.3 | 21.5 | 28.8 | 22.4 | 22.0 | 18.9 | 0.3 | 23.5 | 18.1 | 21.9 | 18.8 | 22.7 | 21.6 | P [ANOVA] | 0.73 | 5.04E-6 | 0.0001 | 1.12E-4 | 1.22E-7 | 9.01E-4 | () | () | () | () | () | () |
| FS [Mpa] | 0 | 314 | 314 | 314 | 314 | 314 | 314 | 0.01 | 260.3 | 214.7 | 354.4 | 290.2 | 363.7 | 257.5 | 0.05 | 171.8 | 226 | 357.3 | 293.4 | 267.9 | 236.6 | 0.1 | 225.6 | 145.5 | 317.6 | 317.6 | 307.5 | 249.5 | 0.3 | 244.9 | 230.5 | 189.6 | 342.9 | 280.5 | 234.3 | P [ANOVA] | 0.001 | 0.02 | 1.17E-8 | 0.1 | 0.02 | 0.7 | () | () | () | () | () | (ï) |
|
LS [%] | 0 | 4 | 4 | 4 | 4 | 4 | 4 | 0.01 | 1.2 | 3.1 | 2.0 | 2.8 | 2.6 | 3.9 | 0.05 | 2.0 | 2.8 | 2.8 | 2.4 | 2.2 | 2.1 | 0.1 | 3.0 | 2.3 | 3.0 | 2.5 | 2.3 | 3.2 | 0.3 | 2.2 | 2.4 | 2.0 | 2.7 | 1.8 | 2.7 | P [ANOVA] | 0.71 | 0.09 | 0.95 | 0.05 | 0.47 | 0.65 | () | () | () | () | () | () |
|
|